<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml">The paper deals with solderability analysis of ITO ceramics (In2O3/SnO2) by metals. SnInAgeTi soft active solder was used for experiments. Solder was actived by power ultrasound in air without flux. The analysis of the interface of phases between solder and ceramics was carried out to determine ultrasonic impact on active metal and identify creation mechanism of joint on the ceramic side.</abstract>

The paper deals with solderability analysis of ITO ceramics (In2O3/SnO2) by metals. SnInAgeTi soft active solder was used for experiments. Solder was actived by power ultrasound in air without flux. The analysis of the interface of phases between solder and ceramics was carried out to determine ultrasonic impact on active metal and identify creation mechanism of joint on the ceramic side.

The Study Into the Transition Areas of a Soldered Joint of ito Ceramics

Department of Welding, Faculty of Materials Science and Technology, Institution of Production Technologies, J. Bottu 25, 917 24 Trnava, Slovak Republic

Research Papers Faculty of Materials Science and Technology Slovak University of Technology

{"article-title":"The Study Into the Transition Areas of a Soldered Joint of ito Ceramics"}

The paper deals with solderability analysis of ITO ceramics (In2O3/SnO2) by metals. SnInAgeTi soft active solder was used for experiments. Solder was actived...

The Study Into the Transition Areas of a Soldered Joint of ito Ceramics

Publié en ligne: 03 mars 2011

Pages: 9 - 15

DOI: https://doi.org/10.2478/v10186-010-0021-3

Mots clés
ultrasonic activation, active solder, ITO (indium-tin oxide) ceramics

This content is open access.

The Study Into the Transition Areas of a Soldered Joint of ito Ceramics

Publié en ligne: 03 mars 2011

Pages: 9 - 15

DOI: https://doi.org/10.2478/v10186-010-0021-3

Mots clésultrasonic activation, active solder, ITO (indium-tin oxide) ceramics

This content is open access.

Mots clés
ultrasonic activation, active solder, ITO (indium-tin oxide) ceramics