<abstract xmlns="http://www.w3.org/1999/xhtml">In this work, we have prepared new materials of the nickel sulfide thin films by using the spray pyrolysis technique for promising co-catalyst to improve the photocatalytic performance or superconductivity. The effect of deposition temperature (523, 573 and 623 K) on structural, optical and electrical properties was investigated. The XRD diffraction shows that the prepared nickel sulfide at 523, 573 and 623 K having an orthorhombic, hexagonal and hexagonal structure, which were Ni3S2, Ni17S18 and NiS2, respectively. The minimum value of crystallite size (45,9 nm) was measured of deposited film at 573K. The thin films prepared at 523 and 573 K have an average transmittance is about 20 %. The prepared Ni1S2 thin film at T=623 K has the lowest calculated optical band gap and Urbach energy. The Ni1S2 thin film also has the best calculated of the refractive index and the extinction coefficient. The FTIR spectrums of the nickel sulfide have various bands such as Ni-S, C-H, O-H, N–H and C-S. The maximum electrical conductivity is 4,29x105 (Ω.cm)−1 was obtained at 573K of the Ni17S18. The nickel sulfide thin films sprayed at 573K have good structural, optical and electrical properties.</abstract>

In this work, we have prepared new materials of the nickel sulfide thin films by using the spray pyrolysis technique for promising co-catalyst to improve the photocatalytic performance or superconductivity. The effect of deposition temperature (523, 573 and 623 K) on structural, optical and electrical properties was investigated. The XRD diffraction shows that the prepared nickel sulfide at 523, 573 and 623 K having an orthorhombic, hexagonal and hexagonal structure, which were Ni3S2, Ni17S18 and NiS2, respectively. The minimum value of crystallite size (45,9 nm) was measured of deposited film at 573K. The thin films prepared at 523 and 573 K have an average transmittance is about 20 %. The prepared Ni1S2 thin film at T=623 K has the lowest calculated optical band gap and Urbach energy. The Ni1S2 thin film also has the best calculated of the refractive index and the extinction coefficient. The FTIR spectrums of the nickel sulfide have various bands such as Ni-S, C-H, O-H, N–H and C-S. The maximum electrical conductivity is 4,29x105 (Ω.cm)−1 was obtained at 573K of the Ni17S18. The nickel sulfide thin films sprayed at 573K have good structural, optical and electrical properties.

Effect of Temperature on the Properties of Nickel Sulfide Films Performed by Spray Pyrolysis Technique

Material Sciences Department, Faculty of Science

Unité de Physique des Dispositifs à Semiconduteurs, Faculté des Sciences de Tunis

Department of Process Engineering, Faculty of Technology

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

In this work, we have prepared new materials of the nickel sulfide thin films by using the spray pyrolysis technique for promising co-catalyst to improve the...

Effect of Temperature on the Properties of Nickel Sulfide Films Performed by Spray Pyrolysis Technique

Data publikacji: 22 wrz 2020

Zakres stron: 36 - 51

DOI: https://doi.org/10.2478/adms-2020-0015

Słowa kluczowe
Nickel sulfide, thin films, spray pyrolysis, optical properties

© 2020 A. Gahtar et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Effect of Temperature on the Properties of Nickel Sulfide Films Performed by Spray Pyrolysis Technique

Data publikacji: 22 wrz 2020

Zakres stron: 36 - 51

DOI: https://doi.org/10.2478/adms-2020-0015

Słowa kluczoweNickel sulfide, thin films, spray pyrolysis, optical properties

© 2020 A. Gahtar et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Słowa kluczowe
Nickel sulfide, thin films, spray pyrolysis, optical properties