This investigation deals with the chemical composition and microstructural analysis of the iron object, a spear excavated from Sanur, Tamil Nadu- a megalithic site dated 300 B.C. to 50 A.D. Phase analysis and microstructural examination were carried using XRD, optical and variable pressure scanning electron microscope (VP-SEM). Optical micrograph shows the equiaxed grain structure along with the Newman bands. Formation of Newman bands suggests that the original artifact was forged at high temperature followed by cooling, although not so rapid to produce the marked hardening. The absence of carbides at the grain boundary, within the grains and lower value of micro-hardness indicates that the iron spear was not subjected to the carburizing treatment. Results of corrosion characterization revealed that deterioration of excavated iron artifact is associated with the presence of chlorine in corrosion products. However,