<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The relation between the results of adhesion and water sensitivity tests was investigated. The tests were performed according to the relevant European standards. Two paving grade bitumens (PGB) with different gradations were used in combination with three adhesion additives and basic, neutral and acidic coarse aggregate. It was concluded that each of the additives enhanced the evaluation of the adhesion regardless of the type of binder and aggregate. All the additives combined with PGB 35/50 improved the water sensitivity results. A better result with PGB 50/70 was observed with only one additive. It was noted that an assessment of the efficiency of an adhesion additive based on a change in the water sensitivity value (ITSR) can contradict a change in the indirect tensile strength. The expected reduction in values with an increase in the coarse aggregate acidity was only confirmed for the adhesion test. The change in the ITSR and the indirect tensile strength of dry and wet samples did not fit the expectations. The correlation between the results of the adhesion and water sensitivity test was low and could not be recommended for predicting the indirect tensile strength of asphalt from rolling bottle test results.</p></abstract>

The relation between the results of adhesion and water sensitivity tests was investigated. The tests were performed according to the relevant European standards. Two paving grade bitumens (PGB) with different gradations were used in combination with three adhesion additives and basic, neutral and acidic coarse aggregate. It was concluded that each of the additives enhanced the evaluation of the adhesion regardless of the type of binder and aggregate. All the additives combined with PGB 35/50 improved the water sensitivity results. A better result with PGB 50/70 was observed with only one additive. It was noted that an assessment of the efficiency of an adhesion additive based on a change in the water sensitivity value (ITSR) can contradict a change in the indirect tensile strength. The expected reduction in values with an increase in the coarse aggregate acidity was only confirmed for the adhesion test. The change in the ITSR and the indirect tensile strength of dry and wet samples did not fit the expectations. The correlation between the results of the adhesion and water sensitivity test was low and could not be recommended for predicting the indirect tensile strength of asphalt from rolling bottle test results.

Investigation of the Relation between Adhesion and Water Sensitivity Test Results

Department of Highway Engineering, Faculty of Civil Engineering

Slovak Journal of Civil Engineering

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The relation between the results of adhesion and water sensitivity tests was investigated. The tests were performed according to the relevant European...

Investigation of the Relation between Adhesion and Water Sensitivity Test Results

Pubblicato online: 31 dic 2019

Pagine: 1 - 6

DOI: https://doi.org/10.2478/sjce-2019-0024

Parole chiave
Binder, Aggregate, Water, Sensitivity, Adhesion, Additive

© 2019 Jozef Komačka et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Investigation of the Relation between Adhesion and Water Sensitivity Test Results

Pubblicato online: 31 dic 2019

Pagine: 1 - 6

DOI: https://doi.org/10.2478/sjce-2019-0024

Parole chiaveBinder, Aggregate, Water, Sensitivity, Adhesion, Additive

© 2019 Jozef Komačka et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Parole chiave
Binder, Aggregate, Water, Sensitivity, Adhesion, Additive