<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Porosity distribution in the spin cast zinc alloy castings was observed. Results shows that it is influenced by rotations per minute and by the centrifugal and Coriolis’ forces. The influence of Coriolis’ force is higher at low rotation speed. Porosity in castings can be eliminated by high rotation speeds.</p></abstract>

Porosity distribution in the spin cast zinc alloy castings was observed. Results shows that it is influenced by rotations per minute and by the centrifugal and Coriolis’ forces. The influence of Coriolis’ force is higher at low rotation speed. Porosity in castings can be eliminated by high rotation speeds.

Study of Porosity Distribution in Spin Cast Zinc Alloy Castings

Slovak University of Technology in Bratislava

Faculty of Materials Science and Technology in Trnava, Institute of Production Technologies

Research Papers Faculty of Materials Science and Technology Slovak University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Study of Porosity Distribution in Spin Cast Zinc Alloy Castings"}

Porosity distribution in the spin cast zinc alloy castings was observed. Results shows that it is influenced by rotations per minute and by the centrifugal and...

Study of Porosity Distribution in Spin Cast Zinc Alloy Castings

Pubblicato online: 04 ott 2018

Pagine: 151 - 158

Ricevuto: 31 mag 2018

Accettato: 12 lug 2018

DOI: https://doi.org/10.2478/rput-2018-0018

Parole chiave
Porosity distribution, spin casting, zinc alloy

© 2018 Martin Bajčičák et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Study of Porosity Distribution in Spin Cast Zinc Alloy Castings

Pubblicato online: 04 ott 2018

Pagine: 151 - 158

Ricevuto: 31 mag 2018

Accettato: 12 lug 2018

DOI: https://doi.org/10.2478/rput-2018-0018

Parole chiavePorosity distribution, spin casting, zinc alloy

© 2018 Martin Bajčičák et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
Porosity distribution, spin casting, zinc alloy