<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Magnesium based alloys are very promising material to be used mainly for biodegradable implants in medical applications. However, due to their very low corrosion resistance in the environment of in vivo is their use limited. Increase of the corrosion resistance of magnesium alloys in vivo can be achieved, for example, by a suitable choice of surface treatment while the biocompatibility must be ensured. Fluoride conversion coatings meet these requirements. Unconventional fluoride conversion coating was prepared on ZE41 magnesium alloy by dipping the magnesium alloy into the Na[BF<sub>4</sub>] salt melt at 450 °C for 0.5; 2 and 8 h. The morphology and thickness of the prepared fluoride conversion coatings were investigated as well as the corrosion resistance of the treated and untreated ZE41 magnesium alloy specimens. The corrosion resistance of the untreated and treated ZE41 magnesium alloy was investigated using electrochemical impedance spectroscopy in the environment of the simulated body fluids at 37 ± 2 °C. The obtained results showed a positive influence of the fluoride conversion coating on the corrosion resistance of the ZE41 magnesium alloy.</p></abstract>

Magnesium based alloys are very promising material to be used mainly for biodegradable implants in medical applications. However, due to their very low corrosion resistance in the environment of in vivo is their use limited. Increase of the corrosion resistance of magnesium alloys in vivo can be achieved, for example, by a suitable choice of surface treatment while the biocompatibility must be ensured. Fluoride conversion coatings meet these requirements. Unconventional fluoride conversion coating was prepared on ZE41 magnesium alloy by dipping the magnesium alloy into the Na[BF4] salt melt at 450 °C for 0.5; 2 and 8 h. The morphology and thickness of the prepared fluoride conversion coatings were investigated as well as the corrosion resistance of the treated and untreated ZE41 magnesium alloy specimens. The corrosion resistance of the untreated and treated ZE41 magnesium alloy was investigated using electrochemical impedance spectroscopy in the environment of the simulated body fluids at 37 ± 2 °C. The obtained results showed a positive influence of the fluoride conversion coating on the corrosion resistance of the ZE41 magnesium alloy.

Corrosion resistance of the biodegradable ZE41 magnesium alloy treated by unconventional fluoride conversion coating

Fakulta strojního inženýrství, Vysoké učení technické

KOM – Corrosion and Material Protection Journal

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Magnesium based alloys are very promising material to be used mainly for biodegradable implants in medical applications. However, due to their very low...

Corrosion resistance of the biodegradable ZE41 magnesium alloy treated by unconventional fluoride conversion coating

Pubblicato online: 24 gen 2020

Pagine: 138 - 147

DOI: https://doi.org/10.2478/kom-2019-0018

© 2019 Drábiková J. et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.