<abstract xmlns="http://www.w3.org/1999/xhtml"><p> Natural diamond has been considered as a perspective material for clinical radiation dosimetry due to its tissuebiocompatibility and chemical inertness. However, the use of natural diamond in radiation dosimetry has been halted by the high market price. The recent progress in the development of CVD techniques for diamond synthesis, offering the capability of growing high quality diamond layers, has renewed the interest in using this material in radiation dosimeters having small geometricalsizes. Polycrystalline CVD diamond films have been proposed as detectors and dosimeters of β and α radiation with prospective applications in high-energy photon dosimetry. In this work, we present a study on the TL properties of undoped diamond film samples grown by the hot filament CVD (HF CVD) method and exposed to β and α radiation. The glow curves for both types of radiation show similar character and can be decomposed into three components. The dominant TL peaks are centered at around 610 K and exhibit activation energy of the order of 0.90 eV. </p></abstract>

Natural diamond has been considered as a perspective material for clinical radiation dosimetry due to its tissuebiocompatibility and chemical inertness. However, the use of natural diamond in radiation dosimetry has been halted by the high market price. The recent progress in the development of CVD techniques for diamond synthesis, offering the capability of growing high quality diamond layers, has renewed the interest in using this material in radiation dosimeters having small geometricalsizes. Polycrystalline CVD diamond films have been proposed as detectors and dosimeters of β and α radiation with prospective applications in high-energy photon dosimetry. In this work, we present a study on the TL properties of undoped diamond film samples grown by the hot filament CVD (HF CVD) method and exposed to β and α radiation. The glow curves for both types of radiation show similar character and can be decomposed into three components. The dominant TL peaks are centered at around 610 K and exhibit activation energy of the order of 0.90 eV.

Thermoluminescence properties of undoped diamond films deposited using HF CVD technique

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Natural diamond has been considered as a perspective material for clinical radiation dosimetry due to its tissuebiocompatibility and chemical inertness....

Thermoluminescence properties of undoped diamond films deposited using HF CVD technique

Pubblicato online: 21 mar 2018

Pagine: 785 - 790

Ricevuto: 09 feb 2017

Accettato: 21 nov 2017

DOI: https://doi.org/10.1515/msp-2017-0103

Parole chiave
HF CVD undoped diamond, thermoluminescence, glow curve deconvolution, Raman scattering

© 2018

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Thermoluminescence properties of undoped diamond films deposited using HF CVD technique

Pubblicato online: 21 mar 2018

Pagine: 785 - 790

Ricevuto: 09 feb 2017

Accettato: 21 nov 2017

DOI: https://doi.org/10.1515/msp-2017-0103

Parole chiaveHF CVD undoped diamond, thermoluminescence, glow curve deconvolution, Raman scattering

© 2018

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Parole chiave
HF CVD undoped diamond, thermoluminescence, glow curve deconvolution, Raman scattering