<abstract xmlns="http://www.w3.org/1999/xhtml"> Efficiency of dye-sensitized solar cell (DSSC) depends on several interrelated factors such as type and concentration of dye, type and thickness of photoelectrode and counter electrode. Optimized combination of these factors leads to a more efficient cell. This paper presents the effect of these parameters on cell efficiency. TiO2 nanoporous thin films of different thicknesses (5 μm to 25 μm) were fabricated on indium doped tin oxide (ITO) coated glass by doctor blading method and characterized by inverted microscope, stylus surface profiler and scanning electron microscope (SEM). Natural organic dye of different concentrations, extracted from turmeric, was prepared with ethanol solvent. Different combinations of dye concentrations and film thicknesses along with different types of carbon catalyst have been investigated by I-V characterization. The result shows that the cell made of a counter electrode catalyst material prepared by candle flame carbon combined with about 15 μm thick photoelectrode and 100 mg/mL dye in ethanol solvent, achieves the highest efficiency of 0.45 %, with open circuit voltage of 566 mV and short circuit current density of 1.02 mA/cm2.</abstract>

Efficiency of dye-sensitized solar cell (DSSC) depends on several interrelated factors such as type and concentration of dye, type and thickness of photoelectrode and counter electrode. Optimized combination of these factors leads to a more efficient cell. This paper presents the effect of these parameters on cell efficiency. TiO2 nanoporous thin films of different thicknesses (5 μm to 25 μm) were fabricated on indium doped tin oxide (ITO) coated glass by doctor blading method and characterized by inverted microscope, stylus surface profiler and scanning electron microscope (SEM). Natural organic dye of different concentrations, extracted from turmeric, was prepared with ethanol solvent. Different combinations of dye concentrations and film thicknesses along with different types of carbon catalyst have been investigated by I-V characterization. The result shows that the cell made of a counter electrode catalyst material prepared by candle flame carbon combined with about 15 μm thick photoelectrode and 100 mg/mL dye in ethanol solvent, achieves the highest efficiency of 0.45 %, with open circuit voltage of 566 mV and short circuit current density of 1.02 mA/cm2.

Efficiency enhancement of natural dye sensitized solar cell by optimizing electrode fabrication parameters

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Efficiency of dye-sensitized solar cell (DSSC) depends on several interrelated factors such as type and concentration of dye, type and thickness of...

Efficiency enhancement of natural dye sensitized solar cell by optimizing electrode fabrication parameters

Pubblicato online: 20 mar 2018

Pagine: 816 - 823

Ricevuto: 23 mar 2017

Accettato: 25 set 2017

DOI: https://doi.org/10.1515/msp-2017-0086

Parole chiave
nanostructured TiO2, DSSC electrode, SEM analysis, surface morphology, cell efficiency

© 2018

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Efficiency enhancement of natural dye sensitized solar cell by optimizing electrode fabrication parameters

Pubblicato online: 20 mar 2018

Pagine: 816 - 823

Ricevuto: 23 mar 2017

Accettato: 25 set 2017

DOI: https://doi.org/10.1515/msp-2017-0086

Parole chiavenanostructured TiO2, DSSC electrode, SEM analysis, surface morphology, cell efficiency

© 2018

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Parole chiave
nanostructured TiO2, DSSC electrode, SEM analysis, surface morphology, cell efficiency