<abstract xmlns="http://www.w3.org/1999/xhtml"> The SEM and EDS results of porous coatings formed on pure titanium by Plasma Electrolytic Oxidation (Micro Arc Oxidation) under DC regime of voltage in the electrolytes containing of 500 g zinc nitrate Zn(NO3)2·6H2O in 1000 mL of concentrated phosphoric acid H3PO4 at three voltages, i.e. 450 V, 550 V, 650 V for 3 minutes, are presented. The PEO coatings with pores, which have different shapes and the diameters, consist mainly of phosphorus, titanium and zinc. The maximum of zinc-to-phosphorus (Zn/P) ratio was found for treatment at 650 V and it equals 0.43 (wt%) | 0.20 (at%), while the minimum of that coefficient was recorded for the voltage of 450 V and equaling 0.26 (wt%) | 0.12 (at%). Performed studies have shown a possible way to form the porous coatings enriched with zinc by Plasma Electrolytic Oxidation in electrolyte containing concentrated phosphoric acid H3PO4 with zinc nitrate Zn(NO3)2·6H2O.</abstract>

The SEM and EDS results of porous coatings formed on pure titanium by Plasma Electrolytic Oxidation (Micro Arc Oxidation) under DC regime of voltage in the electrolytes containing of 500 g zinc nitrate Zn(NO3)2·6H2O in 1000 mL of concentrated phosphoric acid H3PO4 at three voltages, i.e. 450 V, 550 V, 650 V for 3 minutes, are presented. The PEO coatings with pores, which have different shapes and the diameters, consist mainly of phosphorus, titanium and zinc. The maximum of zinc-to-phosphorus (Zn/P) ratio was found for treatment at 650 V and it equals 0.43 (wt%) | 0.20 (at%), while the minimum of that coefficient was recorded for the voltage of 450 V and equaling 0.26 (wt%) | 0.12 (at%). Performed studies have shown a possible way to form the porous coatings enriched with zinc by Plasma Electrolytic Oxidation in electrolyte containing concentrated phosphoric acid H3PO4 with zinc nitrate Zn(NO3)2·6H2O.

SEM and EDS Characterization of Porous Coatings Obtained On Titaniumby Plasma Electrolytic Oxidation in Electrolyte Containing Concentrated Phosphoric Acid with Zinc Nitrate

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The SEM and EDS results of porous coatings formed on pure titanium by Plasma Electrolytic Oxidation (Micro Arc Oxidation) under DC regime of voltage in the...

SEM and EDS Characterization of Porous Coatings Obtained On Titaniumby Plasma Electrolytic Oxidation in Electrolyte Containing Concentrated Phosphoric Acid with Zinc Nitrate

Pubblicato online: 01 ago 2017

Pagine: 41 - 54

DOI: https://doi.org/10.1515/adms-2017-0010

Parole chiave
Plasma Electrolytic Oxidation PEO, Micro Arc Oxidation MAO, SEM, titanium, porous coatings

© by K. Rokosz

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

SEM and EDS Characterization of Porous Coatings Obtained On Titaniumby Plasma Electrolytic Oxidation in Electrolyte Containing Concentrated Phosphoric Acid with Zinc Nitrate

Pubblicato online: 01 ago 2017

Pagine: 41 - 54

DOI: https://doi.org/10.1515/adms-2017-0010

Parole chiavePlasma Electrolytic Oxidation PEO, Micro Arc Oxidation MAO, SEM, titanium, porous coatings

© by K. Rokosz

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Parole chiave
Plasma Electrolytic Oxidation PEO, Micro Arc Oxidation MAO, SEM, titanium, porous coatings