<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Non-alloy quality case-hardening steels are used for low-load components made on automatic machining centers (automatic lines). Because of the widespread use of these steel in open constructions, they are exposed to atmospheric corrosion. The study attempted to analyze the effect of 20% aqueous NaCl solution on the roughness of the steel as a result of corrosion. The steel roughness and corrosion wear were determined according to corrosion time.</p></abstract>

Non-alloy quality case-hardening steels are used for low-load components made on automatic machining centers (automatic lines). Because of the widespread use of these steel in open constructions, they are exposed to atmospheric corrosion. The study attempted to analyze the effect of 20% aqueous NaCl solution on the roughness of the steel as a result of corrosion. The steel roughness and corrosion wear were determined according to corrosion time.

Roughness of 1.0721 steel after corrosion tests in 20% NaCl

University of Warmia and Mazury in Olsztyn

Production Engineering Archives

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Roughness of 1.0721 steel after corrosion tests in 20% NaCl"}

Non-alloy quality case-hardening steels are used for low-load components made on automatic machining centers (automatic lines). Because of the widespread use...

Roughness of 1.0721 steel after corrosion tests in 20% NaCl

Publié en ligne: 28 janv. 2020

Pages: 27 - 30

Reçu: 26 avr. 2017

Accepté: 15 mai 2017

DOI: https://doi.org/10.30657/pea.2017.15.07

Mots clés
steel, corrosion, corrosion rare, roughness, NaCl solution

© 2017 Tomasz Lipiński, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Roughness of 1.0721 steel after corrosion tests in 20% NaCl

Publié en ligne: 28 janv. 2020

Pages: 27 - 30

Reçu: 26 avr. 2017

Accepté: 15 mai 2017

DOI: https://doi.org/10.30657/pea.2017.15.07

Mots cléssteel, corrosion, corrosion rare, roughness, NaCl solution

© 2017 Tomasz Lipiński, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Mots clés
steel, corrosion, corrosion rare, roughness, NaCl solution