<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml">Laminate TiAl3 - titanium alloy composites have unique mechanical properties which result from a combination of the properties of the Ti-Al type intermetallic phases, such as the high stiffness and low density, and the properties of the titanium alloy, primarily its high ductility. These composite materials have already been used in industry, but their application is limited by the low resistance to frictional wear and to oxidation at elevated temperatures. The process of diffusion bonding of titanium alloys with an aluminum foil, followed by magnetron sputtering combined with glow discharge-assisted oxidizing, yields a gradient-type material, i.e. a laminate composite built of the TiAl3-reinforced titanium alloy with a diffusion surface layer of the Al2O3+Ti-Al intermetallic phase type.The paper presents the results of examination of the structure (by optical, SEM and TEM microscopy), phase composition, chemical composition, frictional wear resistance of the Al2O3+TixAly intermetallic composite surface layers produced on the composites, described above, by a duplex method that combines magnetron sputtering and plasma oxidizing processes. The composite surface layers have a diffusion character, and their microstructure, thickness and phase composition can be modified by modifying the parameters of the hybrid process, in particular the parameters of the glow discharge oxidizing, since these decide about whether the structure of the layer is nano-crystalline or fine-grained and thereby about the properties of the laminate composite.</abstract>

Laminate TiAl3 - titanium alloy composites have unique mechanical properties which result from a combination of the properties of the Ti-Al type intermetallic phases, such as the high stiffness and low density, and the properties of the titanium alloy, primarily its high ductility. These composite materials have already been used in industry, but their application is limited by the low resistance to frictional wear and to oxidation at elevated temperatures. The process of diffusion bonding of titanium alloys with an aluminum foil, followed by magnetron sputtering combined with glow discharge-assisted oxidizing, yields a gradient-type material, i.e. a laminate composite built of the TiAl3-reinforced titanium alloy with a diffusion surface layer of the Al2O3+Ti-Al intermetallic phase type.The paper presents the results of examination of the structure (by optical, SEM and TEM microscopy), phase composition, chemical composition, frictional wear resistance of the Al2O3+TixAly intermetallic composite surface layers produced on the composites, described above, by a duplex method that combines magnetron sputtering and plasma oxidizing processes. The composite surface layers have a diffusion character, and their microstructure, thickness and phase composition can be modified by modifying the parameters of the hybrid process, in particular the parameters of the glow discharge oxidizing, since these decide about whether the structure of the layer is nano-crystalline or fine-grained and thereby about the properties of the laminate composite.

Modification of the Microstructure and Properties of Laminate Titanium Alloy - TiAl Intermetallic Phases Composites By A Duplex Surface Engineering Treatment

Faculty of Materials Science and Engineering, Warsaw University of Technology, Warsaw 02-507, Wołoska 141, Poland

AGH University of Science and Technology, Cracow, Poland

Advances in Materials Science

Laminate TiAl3 - titanium alloy composites have unique mechanical properties which result from a combination of the properties of the Ti-Al type intermetallic...

Modification of the Microstructure and Properties of Laminate Titanium Alloy - TiAl Intermetallic Phases Composites By A Duplex Surface Engineering Treatment

Publié en ligne: 20 janv. 2009

Pages: 23 - 31

DOI: https://doi.org/10.2478/v10077-008-0041-2

Mots clés
composites, trialuminides, tribological properties, coatings, wear-resistant applications

This content is open access.

Modification of the Microstructure and Properties of Laminate Titanium Alloy - TiAl Intermetallic Phases Composites By A Duplex Surface Engineering Treatment

Publié en ligne: 20 janv. 2009

Pages: 23 - 31

DOI: https://doi.org/10.2478/v10077-008-0041-2

Mots cléscomposites, trialuminides, tribological properties, coatings, wear-resistant applications

This content is open access.

Mots clés
composites, trialuminides, tribological properties, coatings, wear-resistant applications