Nodular cast irons are used in a wide range of industrial applications, especially in the automotive industry. SiMo-type of nodular cast iron is suitable for high-temperature applications, for example the exhaust manifolds of the combustion engines; SiCu-type of nodular cast iron is used in various components of tribotechnical units. These automotive components often work in a corrosive environment. Therefore, the aim of this paper is to compare the corrosion resistance of two types of the nodular cast irons (SiMo-type and SiCu-type). Corrosion resistance was determined by the exposure immersion test at ambient temperature. Specimens of both types of nodular cast iron were immersed in 3.5 % NaCl solution (to simulate sea water) and gradually removed from the solution after 1, 2, 4 and 8 weeks. Subsequently, the weight loss (g) and the average corrosion rate (g m−2 day−1) were calculated. Experimental results show that nodular cast iron alloyed by Si and Mo has higher corrosion resistance than the nodular cast iron alloyed with Si and Cu. Moreover, the mechanical properties (evaluated by tensile test, impact bending test and hardness test) and fatigue properties of both types of nodular cast iron has been compared in the paper.
</abstract>

Nodular cast irons are used in a wide range of industrial applications, especially in the automotive industry. SiMo-type of nodular cast iron is suitable for high-temperature applications, for example the exhaust manifolds of the combustion engines; SiCu-type of nodular cast iron is used in various components of tribotechnical units. These automotive components often work in a corrosive environment. Therefore, the aim of this paper is to compare the corrosion resistance of two types of the nodular cast irons (SiMo-type and SiCu-type). Corrosion resistance was determined by the exposure immersion test at ambient temperature. Specimens of both types of nodular cast iron were immersed in 3.5 % NaCl solution (to simulate sea water) and gradually removed from the solution after 1, 2, 4 and 8 weeks. Subsequently, the weight loss (g) and the average corrosion rate (g m−2 day−1) were calculated. Experimental results show that nodular cast iron alloyed by Si and Mo has higher corrosion resistance than the nodular cast iron alloyed with Si and Cu. Moreover, the mechanical properties (evaluated by tensile test, impact bending test and hardness test) and fatigue properties of both types of nodular cast iron has been compared in the paper.

Corrosion Resistance of SiMo- and SiCu-Types of Nodular Cast Iron in NaCl Solution

System Safety: Human - Technical Facility - Environment

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Nodular cast irons are used in a wide range of industrial applications, especially in the automotive industry. SiMo-type of nodular cast iron is suitable for...

Corrosion Resistance of SiMo- and SiCu-Types of Nodular Cast Iron in NaCl Solution

Publié en ligne: 18 avr. 2020

Pages: 191 - 198

Reçu: 13 nov. 2019

Accepté: 03 févr. 2020

DOI: https://doi.org/10.2478/czoto-2020-0023

Mots clés
nodular cast iron, corrosion, exposure immersion test, NaCl solution

© 2020 Alan Vaško et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Corrosion Resistance of SiMo- and SiCu-Types of Nodular Cast Iron in NaCl Solution

Publié en ligne: 18 avr. 2020

Pages: 191 - 198

Reçu: 13 nov. 2019

Accepté: 03 févr. 2020

DOI: https://doi.org/10.2478/czoto-2020-0023

Mots clésnodular cast iron, corrosion, exposure immersion test, NaCl solution

© 2020 Alan Vaško et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Mots clés
nodular cast iron, corrosion, exposure immersion test, NaCl solution