<abstract xmlns="http://www.w3.org/1999/xhtml">The aim of the study was to investigate Spark Plasma Sintering (SPS) of 1-3%Mn steels and compare the resultant microstructures, strengths and failure mechanisms with those of conventionally sintered materials. SPS was performed in a vacuum of 5 Pa at 1000°C for 15min under a uniaxial pressure of 20 MPa. The heating rate of 100°C/min was applied. For conventional processing, mixtures of powders were prepared in a Turbula mixer for 30 minutes. Samples were single pressed at 660 MPa, according to PN-EN ISO 2740 standard. Sintering of compacts was carried out in a laboratory tube furnace at 1120°C and 1250°C for 60 minutes in a mixture of 95%N2-5%H2. Heating and cooling rates were 75C°/min and 60°C/min, respectively. The density of SPS samples was higher (up to 7.37 g/cm3) than those after conventional sintering (up to 6.7 g/cm3). Yield strengths of SPS samples were in the range 920-1220 MPa, compared to the maximum of 602 MPa for conventionally sintered Fe-3%Mn-0.8%C. Transverse rupture strengths were the same for this alloy, 1234 MPa, but reached 1473 MPa for SPS 2Mn variant. Interfaces in SPS samples were significantly less contaminated with oxides, which is the result of a more favorable microclimate and pressure acting during SPS. These preliminary results indicate that further research on the SPS of Mn steels is warranted.</abstract>

The aim of the study was to investigate Spark Plasma Sintering (SPS) of 1-3%Mn steels and compare the resultant microstructures, strengths and failure mechanisms with those of conventionally sintered materials. SPS was performed in a vacuum of 5 Pa at 1000°C for 15min under a uniaxial pressure of 20 MPa. The heating rate of 100°C/min was applied. For conventional processing, mixtures of powders were prepared in a Turbula mixer for 30 minutes. Samples were single pressed at 660 MPa, according to PN-EN ISO 2740 standard. Sintering of compacts was carried out in a laboratory tube furnace at 1120°C and 1250°C for 60 minutes in a mixture of 95%N2-5%H2. Heating and cooling rates were 75C°/min and 60°C/min, respectively. The density of SPS samples was higher (up to 7.37 g/cm3) than those after conventional sintering (up to 6.7 g/cm3). Yield strengths of SPS samples were in the range 920-1220 MPa, compared to the maximum of 602 MPa for conventionally sintered Fe-3%Mn-0.8%C. Transverse rupture strengths were the same for this alloy, 1234 MPa, but reached 1473 MPa for SPS 2Mn variant. Interfaces in SPS samples were significantly less contaminated with oxides, which is the result of a more favorable microclimate and pressure acting during SPS. These preliminary results indicate that further research on the SPS of Mn steels is warranted.

Density, Microstructure, Strength and Fractography of Spark Plasma and Conventionally Sintered Mn Steels

Faculty of Metals Engineering and Industrial Computer Science

Institute of Materials Research, Slovak Academy of Sciences

Powder Metallurgy Progress

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The aim of the study was to investigate Spark Plasma Sintering (SPS) of 1-3%Mn steels and compare the resultant microstructures, strengths and failure...

Density, Microstructure, Strength and Fractography of Spark Plasma and Conventionally Sintered Mn Steels

Publié en ligne: 01 mars 2018

Pages: 93 - 103

DOI: https://doi.org/10.1515/pmp-2017-0010

Mots clés
Spark Plasma Sintering (SPS), sintered steels, mechanical properties

© 2017 M. Tenerowicz-Zaba et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Density, Microstructure, Strength and Fractography of Spark Plasma and Conventionally Sintered Mn Steels

Publié en ligne: 01 mars 2018

Pages: 93 - 103

DOI: https://doi.org/10.1515/pmp-2017-0010

Mots clésSpark Plasma Sintering (SPS), sintered steels, mechanical properties

© 2017 M. Tenerowicz-Zaba et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Mots clés
Spark Plasma Sintering (SPS), sintered steels, mechanical properties