<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Single crystals of pure and L-threonine added tartaric acid (LT/TA), organic nonlinear optical (NLO) materials were grown from their respective aqueous solution by slow evaporation method. The crystalline nature of the grown crystals was confirmed by powder X-ray diffraction analysis (XRD). UV-Vis-NIR absorption and transmission spectra revealed that the lower cut-off wavelength was around 281 nm and the crystals exhibited high transmission over visible and near IR region. The presence of the functional groups such as O–H, C–H, C–O, C=O in the grown crystals was confirmed by FT-IR analysis. CHN analysis was carried out to confirm the presence of L-threonine in the grown crystals. Microhardness study on the crystals revealed that the hardness number H<italic><sub>v</sub></italic> increased with the applied load. The growth pattern of the crystals were analyzed through etching analysis from which the etch patterns in the shape of ‘step-triangle’ were observed. The second harmonic generation (SHG) properties of pure and L-threonine doped tartaric acid crystals were confirmed by Kurtz-Perry powder technique.</p></abstract>

Single crystals of pure and L-threonine added tartaric acid (LT/TA), organic nonlinear optical (NLO) materials were grown from their respective aqueous solution by slow evaporation method. The crystalline nature of the grown crystals was confirmed by powder X-ray diffraction analysis (XRD). UV-Vis-NIR absorption and transmission spectra revealed that the lower cut-off wavelength was around 281 nm and the crystals exhibited high transmission over visible and near IR region. The presence of the functional groups such as O–H, C–H, C–O, C=O in the grown crystals was confirmed by FT-IR analysis. CHN analysis was carried out to confirm the presence of L-threonine in the grown crystals. Microhardness study on the crystals revealed that the hardness number Hv increased with the applied load. The growth pattern of the crystals were analyzed through etching analysis from which the etch patterns in the shape of ‘step-triangle’ were observed. The second harmonic generation (SHG) properties of pure and L-threonine doped tartaric acid crystals were confirmed by Kurtz-Perry powder technique.

Influence of L-threonine on the growth, structural, optical, mechanical and nonlinear optical properties of tartaric acid single crystal

Department of Physics, Dr. N.G.P. Institute of Technology

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Single crystals of pure and L-threonine added tartaric acid (LT/TA), organic nonlinear optical (NLO) materials were grown from their respective aqueous...

Influence of L-threonine on the growth, structural, optical, mechanical and nonlinear optical properties of tartaric acid single crystal

Publicado en línea: 01 feb 2019

Páginas: 630 - 637

Recibido: 17 jul 2017

Aceptado: 13 oct 2018

DOI: https://doi.org/10.2478/msp-2018-0094

Palabras clave
crystal growth, optical materials, growth from solutions, X-ray diffraction

© 2018 G. Thilakavathi et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Influence of L-threonine on the growth, structural, optical, mechanical and nonlinear optical properties of tartaric acid single crystal

Publicado en línea: 01 feb 2019

Páginas: 630 - 637

Recibido: 17 jul 2017

Aceptado: 13 oct 2018

DOI: https://doi.org/10.2478/msp-2018-0094

Palabras clavecrystal growth, optical materials, growth from solutions, X-ray diffraction

© 2018 G. Thilakavathi et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Palabras clave
crystal growth, optical materials, growth from solutions, X-ray diffraction