<abstract xmlns="http://www.w3.org/1999/xhtml">This paper deals with the behaviour of cement paste upon the addition of crushed polystyrene foam. Crushed polystyrene foam waste with a fill density of 13.97 kg/m3 and hydrated lime were used to prepare the foam. Three different types of samples S-1, S-2, and S-3 were prepared to observe the behaviour of cement pastes after the addition of different doses of foam in constant water/cement ratio. The volumetric ratio of EPS and cement paste were 1: 1.294; 1: 0.863; and 1: 0.647. In each type of sample, 0.28 water/cement ratio is maintained. Slump test was carried out in the fresh state and it has been found slump value was decreasing by increasing foam content in concrete sample. On the 7th and 28th day of curing process, the compressive strength test was carried out. Compressive strength and density of concrete samples also decreasing by addition of higher foam content. In addition, water absorption test and microscopic analysis tests were carried out on the 28th day of curing process. It has been found from the study that samples thermal conductivity is working proportionally.</abstract>

This paper deals with the behaviour of cement paste upon the addition of crushed polystyrene foam. Crushed polystyrene foam waste with a fill density of 13.97 kg/m3 and hydrated lime were used to prepare the foam. Three different types of samples S-1, S-2, and S-3 were prepared to observe the behaviour of cement pastes after the addition of different doses of foam in constant water/cement ratio. The volumetric ratio of EPS and cement paste were 1: 1.294; 1: 0.863; and 1: 0.647. In each type of sample, 0.28 water/cement ratio is maintained. Slump test was carried out in the fresh state and it has been found slump value was decreasing by increasing foam content in concrete sample. On the 7th and 28th day of curing process, the compressive strength test was carried out. Compressive strength and density of concrete samples also decreasing by addition of higher foam content. In addition, water absorption test and microscopic analysis tests were carried out on the 28th day of curing process. It has been found from the study that samples thermal conductivity is working proportionally.

Investigations of the Influence of Polystyrene Foamed Granules on the Properties of Lightweight Concrete

Journal of Applied Engineering Sciences

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

This paper deals with the behaviour of cement paste upon the addition of crushed polystyrene foam. Crushed polystyrene foam waste with a fill density of 13.97...

Investigations of the Influence of Polystyrene Foamed Granules on the Properties of Lightweight Concrete

Publicado en línea: 25 jul 2019

Páginas: 19 - 24

Recibido: 24 dic 2018

Aceptado: 14 mar 2019

DOI: https://doi.org/10.2478/jaes-2019-0002

Palabras clave
Lightweight concrete, thermal conductivity, polystyrene foam concrete, Microscopic analysis

© 2019 Adhikary Suman Kumar et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Investigations of the Influence of Polystyrene Foamed Granules on the Properties of Lightweight Concrete

Publicado en línea: 25 jul 2019

Páginas: 19 - 24

Recibido: 24 dic 2018

Aceptado: 14 mar 2019

DOI: https://doi.org/10.2478/jaes-2019-0002

Palabras claveLightweight concrete, thermal conductivity, polystyrene foam concrete, Microscopic analysis

© 2019 Adhikary Suman Kumar et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
Lightweight concrete, thermal conductivity, polystyrene foam concrete, Microscopic analysis