<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Wet welding is the most common method of welding in water environment. It is most often used for repairing of underwater parts of offshore structures. However, the water as a welding environment causes an increase of susceptibility of steels to cold cracking. For underwater constructions high strength low alloy (HSLA) steel are widely used. In wet welding condition a HSLA steel is characterized by high susceptibility to cold cracking. Temper Bead Welding (TBW) was chosen as a method to improve the weldability of S460N steel. The studies showed that TBW technique causes significant decrease of maximum hardness of heat affected zone (HAZ). The largest decrease in hardness occurred in specimens with the pitches in range 66-100%.</p></abstract>

Wet welding is the most common method of welding in water environment. It is most often used for repairing of underwater parts of offshore structures. However, the water as a welding environment causes an increase of susceptibility of steels to cold cracking. For underwater constructions high strength low alloy (HSLA) steel are widely used. In wet welding condition a HSLA steel is characterized by high susceptibility to cold cracking. Temper Bead Welding (TBW) was chosen as a method to improve the weldability of S460N steel. The studies showed that TBW technique causes significant decrease of maximum hardness of heat affected zone (HAZ). The largest decrease in hardness occurred in specimens with the pitches in range 66-100%.

Temper Bead Welding of S460N Steel in Wet Welding Conditions

Faculty of Mechanical Engineering, Department of Materials Science and Welding Engineering

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Temper Bead Welding of S460N Steel in Wet Welding Conditions"}

Wet welding is the most common method of welding in water environment. It is most often used for repairing of underwater parts of offshore structures. However,...

Temper Bead Welding of S460N Steel in Wet Welding Conditions

Publicado en línea: 29 oct 2018

Páginas: 5 - 14

DOI: https://doi.org/10.1515/adms-2017-0036

Palabras clave
temper bead welding, underwater welding, covered electrodes, weldability, cold cracking

© 2018 J. Tomków et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Temper Bead Welding of S460N Steel in Wet Welding Conditions

Publicado en línea: 29 oct 2018

Páginas: 5 - 14

DOI: https://doi.org/10.1515/adms-2017-0036

Palabras clavetemper bead welding, underwater welding, covered electrodes, weldability, cold cracking

© 2018 J. Tomków et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
temper bead welding, underwater welding, covered electrodes, weldability, cold cracking