<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>The structure and dielectric properties of perovskite Ag(Nb0.8Ta0.2)O3 ceramics were explored. A small amount of Bi2O3 was used to modify the dielectric properties of the ceramics. The addition of Bi2O3 led the ceramics to a high densification and optimal dielectric properties. With the addition of 4.5 wt% Bi2O3, the permittivity of Ag(Nb0.8Ta0.2)O3 ceramics increased from 470 to 733, the dielectric loss decreased from 62×10−4 to 6.7×10−4, and the temperature coefficient of capacitance, TCC, decreased from 2004 ppm/°C to −50 ppm/°C. The high permittivity obtained was due to the high densification and weak Ta-O or Nb-O bond strength in the oxygen octahedron that results from the addition of Bi2O3.</p></abstract>

The structure and dielectric properties of perovskite Ag(Nb0.8Ta0.2)O3 ceramics were explored. A small amount of Bi2O3 was used to modify the dielectric properties of the ceramics. The addition of Bi2O3 led the ceramics to a high densification and optimal dielectric properties. With the addition of 4.5 wt% Bi2O3, the permittivity of Ag(Nb0.8Ta0.2)O3 ceramics increased from 470 to 733, the dielectric loss decreased from 62×10−4 to 6.7×10−4, and the temperature coefficient of capacitance, TCC, decreased from 2004 ppm/°C to −50 ppm/°C. The high permittivity obtained was due to the high densification and weak Ta-O or Nb-O bond strength in the oxygen octahedron that results from the addition of Bi2O3.

Influence of Bi2O3 addition on structure and dielectric properties of Ag(Nb0.8Ta0.2)O3 ceramics

School of Electronic and Information Engineering, Tianjin University, Tianjin, 300072, China

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The structure and dielectric properties of perovskite Ag(Nb0.8Ta0.2)O3 ceramics were explored. A small amount of Bi2O3 was used to modify the dielectric...

Influence of Bi2O3 addition on structure and dielectric properties of Ag(Nb0.8Ta0.2)O3 ceramics

Online veröffentlicht: 03. Aug. 2011

Seitenbereich: 1 - 8

DOI: https://doi.org/10.2478/s13536-011-0002-z

Schlüsselwörter
Ag(Nb0.8Ta0.2)O3 ceramics, Bi2O3, dielectric properties, high permittivity, low dielectric loss

© 2011 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Influence of Bi2O3 addition on structure and dielectric properties of Ag(Nb0.8Ta0.2)O3 ceramics

Online veröffentlicht: 03. Aug. 2011

Seitenbereich: 1 - 8

DOI: https://doi.org/10.2478/s13536-011-0002-z

SchlüsselwörterAg(Nb0.8Ta0.2)O3 ceramics, Bi2O3, dielectric properties, high permittivity, low dielectric loss

© 2011 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
Ag(Nb0.8Ta0.2)O3 ceramics, Bi2O3, dielectric properties, high permittivity, low dielectric loss