<abstract xmlns="http://www.w3.org/1999/xhtml"><p>A poly(hydroxybutyl citrate) p(HBC) was obtained. The product compound produced in the solution during esterification, was added to rigid polyurethane-polyisocyanurate foams (PUR-PIR). The amount of petrochemical polyol in the foams was decreased in favor of the p(HBC) from 0.1 to 0.5 equivalent. The foams were foamed in two ways: with distilled water (W foams) and with Solkane 365/227 (S foams). The examination results of both foam series were compared. They showed that the foams foamed with water have higher softening temperature than the foams foamed with solkane. The retention values for both foam series are around 91–95%, and water absorption in the range of 0.7–3.2%. The anisotropy coefficient did not exceed 1.08 (the lowest value being 1.01).</p></abstract>

A poly(hydroxybutyl citrate) p(HBC) was obtained. The product compound produced in the solution during esterification, was added to rigid polyurethane-polyisocyanurate foams (PUR-PIR). The amount of petrochemical polyol in the foams was decreased in favor of the p(HBC) from 0.1 to 0.5 equivalent. The foams were foamed in two ways: with distilled water (W foams) and with Solkane 365/227 (S foams). The examination results of both foam series were compared. They showed that the foams foamed with water have higher softening temperature than the foams foamed with solkane. The retention values for both foam series are around 91–95%, and water absorption in the range of 0.7–3.2%. The anisotropy coefficient did not exceed 1.08 (the lowest value being 1.01).

PUR-PIR foam produced based on poly(hydroxybutyl citrate) foamed founded with different factories

Polish Journal of Chemical Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

A poly(hydroxybutyl citrate) p(HBC) was obtained. The product compound produced in the solution during esterification, was added to rigid...

PUR-PIR foam produced based on poly(hydroxybutyl citrate) foamed founded with different factories

Online veröffentlicht: 16. Apr. 2018

Seitenbereich: 87 - 95

DOI: https://doi.org/10.2478/pjct-2018-0013

Schlüsselwörter
rigid foam, polyurethane, polyol, citric acid, condensation

© 2018 Joanna Liszkowska et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

PUR-PIR foam produced based on poly(hydroxybutyl citrate) foamed founded with different factories

Online veröffentlicht: 16. Apr. 2018

Seitenbereich: 87 - 95

DOI: https://doi.org/10.2478/pjct-2018-0013

Schlüsselwörterrigid foam, polyurethane, polyol, citric acid, condensation

© 2018 Joanna Liszkowska et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
rigid foam, polyurethane, polyol, citric acid, condensation