<abstract xmlns="http://www.w3.org/1999/xhtml">Ion implantation has a potential to modify the surface properties and to produce thin conductive layers in insulating polymers. For this purpose, poly-allyl-diglycol-carbonate (CR-39) was implanted by 400 keV Au+ ions with ion fluences ranging from 5 × 1013 ions/cm2 to 5 × 1015 ions/cm2. The chemical, morphological and optical properties of implanted CR-39 were analyzed using Raman, Fourier transform infrared (FT-IR) spectroscopy, atomic force microscopy (AFM) and UV-Vis spectroscopy. The electrical conductivity of implanted samples was determined through four-point probe technique. Raman spectroscopy revealed the formation of carbonaceous structures in the implanted layer of CR-39. From FT-IR spectroscopy analysis, changes in functional groups of CR-39 after ion implantation were observed. AFM studies revealed that morphology and surface roughness of implanted samples depend on the fluence of Au ions. The optical band gap of implanted samples decreased from 3.15 eV (for pristine) to 1.05 eV (for sample implanted at 5 × 1015 ions/cm2). The electrical conductivity was observed to increase with the ion fluence. It is suggested that due to an increase in ion fluence, the carbonaceous structures formed in the implanted region are responsible for the increase in electrical conductivity.</abstract>

Ion implantation has a potential to modify the surface properties and to produce thin conductive layers in insulating polymers. For this purpose, poly-allyl-diglycol-carbonate (CR-39) was implanted by 400 keV Au+ ions with ion fluences ranging from 5 × 1013 ions/cm2 to 5 × 1015 ions/cm2. The chemical, morphological and optical properties of implanted CR-39 were analyzed using Raman, Fourier transform infrared (FT-IR) spectroscopy, atomic force microscopy (AFM) and UV-Vis spectroscopy. The electrical conductivity of implanted samples was determined through four-point probe technique. Raman spectroscopy revealed the formation of carbonaceous structures in the implanted layer of CR-39. From FT-IR spectroscopy analysis, changes in functional groups of CR-39 after ion implantation were observed. AFM studies revealed that morphology and surface roughness of implanted samples depend on the fluence of Au ions. The optical band gap of implanted samples decreased from 3.15 eV (for pristine) to 1.05 eV (for sample implanted at 5 × 1015 ions/cm2). The electrical conductivity was observed to increase with the ion fluence. It is suggested that due to an increase in ion fluence, the carbonaceous structures formed in the implanted region are responsible for the increase in electrical conductivity.

Modification in surface properties of poly-allyl-diglycol-carbonate (CR-39) implanted by Au+ ions at different fluences

Physics Department, Lahore College for Women University, Lahore, 54000, Pakistan

Physics Department, University of Engineering and Technology, Lahore, 54000, Pakistan

Michigan Ion Beam Laboratory, University of Michigan, Ann Arbor, MI, 48109-2104, USA

National Institute of Lasers and Optronics (NILOP), P.O. Nilore, Islamabad, Pakistan

Chemistry Department, Lahore University of Management Sciences, Lahore, Pakistan

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Modification in surface properties of poly-allyl-diglycol-carbonate (CR-39) implanted by Au ions at different fluences

Ion implantation has a potential to modify the surface properties and to produce thin conductive layers in insulating polymers. For this purpose,...

Modification in surface properties of poly-allyl-diglycol-carbonate (CR-39) implanted by Au⁺ ions at different fluences

Article Category: Research Article

Online veröffentlicht: 27. Juni 2016

Seitenbereich: 468 - 478

Eingereicht: 30. Aug. 2015

Akzeptiert: 20. Mai 2016

DOI: https://doi.org/10.1515/msp-2016-0067

© Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.