<abstract xmlns="http://www.w3.org/1999/xhtml">Bismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO4 ceramics was fabricated by mixed oxide method and sintered at temperature <italic>T</italic>&lt;1000°C. As the sintering aids a small amount of CuO oxide was used. The crystalline structure of the ceramic samples was examined by X-ray diffraction method at room temperature. The Rietveld refinement method was used for analysis of diffraction data. As a result an influence of dopants on crystal structure of bismuth niobate (BiNbO4) ceramics was revealed. It was found that fabricated BiNbO4 ceramics adopted the orthorhombic symmetry (<italic>α</italic>-BiNbO4 phase, <italic>Pnna</italic> (52) space group). Small differences in elementary cell parameters were found.</abstract>

Bismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO4 ceramics was fabricated by mixed oxide method and sintered at temperature T<1000°C. As the sintering aids a small amount of CuO oxide was used. The crystalline structure of the ceramic samples was examined by X-ray diffraction method at room temperature. The Rietveld refinement method was used for analysis of diffraction data. As a result an influence of dopants on crystal structure of bismuth niobate (BiNbO4) ceramics was revealed. It was found that fabricated BiNbO4 ceramics adopted the orthorhombic symmetry (α-BiNbO4 phase, Pnna (52) space group). Small differences in elementary cell parameters were found.

Influence of Dopants on Structure of Polycrystalline Bismuth Niobate

Faculty of Mechanical Engineering, Department of Materials Engineering and Welding

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Influence of Dopants on Structure of Polycrystalline Bismuth Niobate"}

Bismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO4 ceramics was fabricated by...

Influence of Dopants on Structure of Polycrystalline Bismuth Niobate

Online veröffentlicht: 03. Jan. 2019

Seitenbereich: 35 - 41

DOI: https://doi.org/10.1515/adms-2017-0048

Schlüsselwörter
BiNbO ceramics, X-ray diffraction, phase analysis, crystal structure

© 2018 D. Czekaj et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Influence of Dopants on Structure of Polycrystalline Bismuth Niobate

Online veröffentlicht: 03. Jan. 2019

Seitenbereich: 35 - 41

DOI: https://doi.org/10.1515/adms-2017-0048

SchlüsselwörterBiNbO ceramics, X-ray diffraction, phase analysis, crystal structure

© 2018 D. Czekaj et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
BiNbO ceramics, X-ray diffraction, phase analysis, crystal structure