<abstract xmlns="http://www.w3.org/1999/xhtml"> In this attempt, segmented poly(urethane urea) was prepared from polycaprolactone triol (soft segment), 1,3- bis(isocyanatomethyl)cyclohexane (hard segment) and 4,5-diaminophthalonitrile (chain extender). Acidfunctionalized nano-diamond was used as nano-filler. The nanocomposites were processed using solution casting and melt blending. Unique morphology was observed by SEM due to generation of crosslinked polyurethane and ND network. The s-PUU/ND 10 depicted 6 % increase in tensile strength compared with m-PUU/ND 10. 10 wt. % ND loading via solution route increased conductivity to 0.089 Scm-1 relative to m-PUU/ND 10 (0.057 Scm-1). Electrical conductivity of nanocomposites was enough to show electroactive shape recovery of 95 % (40 V).</abstract>

In this attempt, segmented poly(urethane urea) was prepared from polycaprolactone triol (soft segment), 1,3- bis(isocyanatomethyl)cyclohexane (hard segment) and 4,5-diaminophthalonitrile (chain extender). Acidfunctionalized nano-diamond was used as nano-filler. The nanocomposites were processed using solution casting and melt blending. Unique morphology was observed by SEM due to generation of crosslinked polyurethane and ND network. The s-PUU/ND 10 depicted 6 % increase in tensile strength compared with m-PUU/ND 10. 10 wt. % ND loading via solution route increased conductivity to 0.089 Scm-1 relative to m-PUU/ND 10 (0.057 Scm-1). Electrical conductivity of nanocomposites was enough to show electroactive shape recovery of 95 % (40 V).

Effect of Nanofiller Dispersion on Morphology, Mechanical and Conducting Properties of Electroactive Shape Memory Poly(Urethane-Urea)/Functional Nanodiamond Composite

Nanosciences and Catalysis Division, National Centre For Physics, Quaid-i-Azam University Campus, 44000, Islamabad, Pakistan

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

In this attempt, segmented poly(urethane urea) was prepared from polycaprolactone triol (soft segment), 1,3- bis(isocyanatomethyl)cyclohexane (hard segment)...

Effect of Nanofiller Dispersion on Morphology, Mechanical and Conducting Properties of Electroactive Shape Memory Poly(Urethane-Urea)/Functional Nanodiamond Composite

Online veröffentlicht: 30. Dez. 2015

Seitenbereich: 14 - 28

DOI: https://doi.org/10.1515/adms-2015-0019

Schlüsselwörter
Poly(urethane urea), nanodiamond, electroactive shape recovery

© by A. Kausar

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Effect of Nanofiller Dispersion on Morphology, Mechanical and Conducting Properties of Electroactive Shape Memory Poly(Urethane-Urea)/Functional Nanodiamond Composite

Online veröffentlicht: 30. Dez. 2015

Seitenbereich: 14 - 28

DOI: https://doi.org/10.1515/adms-2015-0019

SchlüsselwörterPoly(urethane urea), nanodiamond, electroactive shape recovery

© by A. Kausar

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
Poly(urethane urea), nanodiamond, electroactive shape recovery