<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The paper presents the laboratory measurements results of temperature distribution in the cutting zone during orthogonal turning of a GrDe 2 titanium tube. The cutting tool used during the tests was a bimetallic cut-off tool with an uncoated insert made of P10 sintered carbide. The test plan was developed using the miniTab16 computer application and the Taguchi method. The tests were performed in accordance with orthogonal table l9, which describes nine cutting trials for two independent factors, cutting speed <italic>v</italic><italic><sub>c</sub></italic> [m/min] and feed rate <italic>f</italic> [mm/rev], at three different values. The temperature distribution in the cutting zone was measured by means of a flIr sC 620 thermal imaging camera. The archiving and processing of measurement results was performed with the ThermaCamresearcher Pro 2.9 computer application. The obtained results were used to determine the average temperature for each of the nine trials; then, a statistical analysis of the results was performed.</p></abstract>

The paper presents the laboratory measurements results of temperature distribution in the cutting zone during orthogonal turning of a GrDe 2 titanium tube. The cutting tool used during the tests was a bimetallic cut-off tool with an uncoated insert made of P10 sintered carbide. The test plan was developed using the miniTab16 computer application and the Taguchi method. The tests were performed in accordance with orthogonal table l9, which describes nine cutting trials for two independent factors, cutting speed vc [m/min] and feed rate f [mm/rev], at three different values. The temperature distribution in the cutting zone was measured by means of a flIr sC 620 thermal imaging camera. The archiving and processing of measurement results was performed with the ThermaCamresearcher Pro 2.9 computer application. The obtained results were used to determine the average temperature for each of the nine trials; then, a statistical analysis of the results was performed.

Experimental determination of the temperature in the cutting zone during turning of titanium alloy grade 2

Institute of Production Engineering, Faculty of Mechanical Engineering

Technical Transactions

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 Public License.

The paper presents the laboratory measurements results of temperature distribution in the cutting zone during orthogonal turning of a GrDe 2 titanium tube. The...

Experimental determination of the temperature in the cutting zone during turning of titanium alloy grade 2

Published Online: May 21, 2020

Page range: 189 - 197

Received: Aug 03, 2018

DOI: https://doi.org/10.4467/2353737XCT.18.125.8900

Keywords
GRADE 2, temperature, thermovision camera

© 2019 Łukasz Ślusarczyk et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 Public License.

Experimental determination of the temperature in the cutting zone during turning of titanium alloy grade 2

Published Online: May 21, 2020

Page range: 189 - 197

Received: Aug 03, 2018

DOI: https://doi.org/10.4467/2353737XCT.18.125.8900

KeywordsGRADE 2, temperature, thermovision camera

© 2019 Łukasz Ślusarczyk et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 Public License.

Keywords
GRADE 2, temperature, thermovision camera