Electrical properties for cold sprayed Nano copper oxide thin films

This work is a Copper oxide (CuO) thin films were effectively produced using cold spray technique. The process take place in an inert gas (helium) without using catalyst. Nano CuO was deposited on a glass slide, using helium as carrier gas heated to 100, 200, 300, and 400 °C, respectively on heated glass substrates at 300°C. The effect of structural and electrical properties was examined at each temperature for each film. AFM images show that the CuO thin film have different diameters ranging from 80 to 600 nm, and low surface roughness about 20.9 nm. The measured value of copper oxide resistivity was found to be decrease very much with the increasing temperature. All the result showed that copper oxide is suitable material for photovoltaic applications. This research is part of a larger work for the solar cells industry. Therefore, the aim of this research is to study the electrical properties of solar cells in the primary stages of manufacturing from available materials at low costs.