<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The article deals with a reduction of friction coefficient of bearing steel 100Cr6. Reduction of friction was achieved by means of a CarbonX DLC coating. The coating exhibited excellent friction and mechanical properties. This coating was applied to samples made of 100Cr6 bearing steel. The friction results of the CarbonX coating were compared to the friction results of the 100Cr6 bearing steel. Reducing the friction of 100Cr6 bearing steel resulted in reduced wear and increase lifetime. The friction process of the samples will take place in an environment without lubrication. The aim of the article is to verify the behaviour of the DLC coating without the presence of lubricant in the friction node. The achieved results are to be interpreted in the conclusion of article.</p></abstract>

The article deals with a reduction of friction coefficient of bearing steel 100Cr6. Reduction of friction was achieved by means of a CarbonX DLC coating. The coating exhibited excellent friction and mechanical properties. This coating was applied to samples made of 100Cr6 bearing steel. The friction results of the CarbonX coating were compared to the friction results of the 100Cr6 bearing steel. Reducing the friction of 100Cr6 bearing steel resulted in reduced wear and increase lifetime. The friction process of the samples will take place in an environment without lubrication. The aim of the article is to verify the behaviour of the DLC coating without the presence of lubricant in the friction node. The achieved results are to be interpreted in the conclusion of article.

Investigation of tribological properties of CarbonX coating deposited on 100Cr6 steel

Production Engineering Archives

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The article deals with a reduction of friction coefficient of bearing steel 100Cr6. Reduction of friction was achieved by means of a CarbonX DLC coating. The...

Investigation of tribological properties of CarbonX coating deposited on 100Cr6 steel

Published Online: Dec 30, 2019

Page range: 52 - 55

Received: Sep 23, 2019

Accepted: Nov 15, 2019

DOI: https://doi.org/10.30657/pea.2019.25.10

Keywords
tribology, DLC coating, 100Cr6 steel, friction

© 2019 Martin Vicen et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Investigation of tribological properties of CarbonX coating deposited on 100Cr6 steel

Published Online: Dec 30, 2019

Page range: 52 - 55

Received: Sep 23, 2019

Accepted: Nov 15, 2019

DOI: https://doi.org/10.30657/pea.2019.25.10

Keywordstribology, DLC coating, 100Cr6 steel, friction

© 2019 Martin Vicen et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Keywords
tribology, DLC coating, 100Cr6 steel, friction