<abstract xmlns="http://www.w3.org/1999/xhtml">In the present paper, TL and PL study of Dy3+ doped Sr2SiO4:Eu2+ phosphor is reported. A polycrystalline sample of Sr2SiO4:Eu2+, Dy3+ was prepared by combustion method. The obtained phosphor was characterized by powder X-ray diffraction, scanning electron microscopy, UV-Vis spectroscopy, PL and thermoluminescence. The results of the XRD studies obtained for Sr2SiO4:Eu2+, Dy3+ phosphor revealed its monoclinic structure. The average crystallite size was calculated as 12.77 nm. Thermoluminescence study was carried out for the phosphor using UV irradiation and a single glow peak was found. The thermoluminescence glow curves of the samples were measured at various concentrations of co-dopant. The kinetic parameter has been calculated using Chen’s glow curve method. In this paper, the photoluminescence and afterglow behavior of these phosphors are reported.</abstract>

In the present paper, TL and PL study of Dy3+ doped Sr2SiO4:Eu2+ phosphor is reported. A polycrystalline sample of Sr2SiO4:Eu2+, Dy3+ was prepared by combustion method. The obtained phosphor was characterized by powder X-ray diffraction, scanning electron microscopy, UV-Vis spectroscopy, PL and thermoluminescence. The results of the XRD studies obtained for Sr2SiO4:Eu2+, Dy3+ phosphor revealed its monoclinic structure. The average crystallite size was calculated as 12.77 nm. Thermoluminescence study was carried out for the phosphor using UV irradiation and a single glow peak was found. The thermoluminescence glow curves of the samples were measured at various concentrations of co-dopant. The kinetic parameter has been calculated using Chen’s glow curve method. In this paper, the photoluminescence and afterglow behavior of these phosphors are reported.

Optical properties of Sr2SiO4:Eu2+, Dy3+ phosphors prepared by combustion method

Department of Applied Physics, Faculty of Engineering and Technology, Shri Shankaracharya Group of Institutions, Shri Shankaracharya Technical Campus

Department of Applied Physics, Professional Institute of Engineering and Technology

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Optical properties of SrSiO:Eu, Dy phosphors prepared by combustion method

In the present paper, TL and PL study of Dy3+ doped Sr2SiO4:Eu2+ phosphor is reported. A polycrystalline sample of Sr2SiO4:Eu2+, Dy3+ was prepared by...

Optical properties of Sr₂SiO₄:Eu²⁺, Dy³⁺ phosphors prepared by combustion method

Published Online: Nov 02, 2018

Page range: 387 - 396

Received: Mar 16, 2017

Accepted: Feb 19, 2017

DOI: https://doi.org/10.1515/msp-2018-0029

Keywords
thermoluminescence, combustion method, XRD, photoluminescence

© 2018 Durga Verma et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Optical properties of Sr2SiO4:Eu2+, Dy3+ phosphors prepared by combustion method

Published Online: Nov 02, 2018

Page range: 387 - 396

Received: Mar 16, 2017

Accepted: Feb 19, 2017

DOI: https://doi.org/10.1515/msp-2018-0029

Keywordsthermoluminescence, combustion method, XRD, photoluminescence

© 2018 Durga Verma et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Optical properties of Sr₂SiO₄:Eu²⁺, Dy³⁺ phosphors prepared by combustion method

Keywords
thermoluminescence, combustion method, XRD, photoluminescence