<abstract xmlns="http://www.w3.org/1999/xhtml"> The influence of vanadium dioxide VO2(B) on thermal decomposition of ammonium perchlorate (AP) has not been reported before. In this contribution, the effect of VO2(B) nanobelts on the thermal decomposition of AP was investigated by the Thermo- Gravimetric Analysis and Differential Thermal Analysis (TG/DTA). VO2(B) nanobelts were hydrothermally prepared using peroxovanadium (V) complexes, ethanol and water as starting materials. The thermal decomposition temperatures of AP in the presence of I wt.%, 3 wt.% and 6 wt.% of as-obtained VO2&lt;B) nanobelts were reduced by 39 °C. 62 °C and 74 °C, respectively. The results indicated that VO2(B) nanobelts had a great influence on the thermal decomposition temperature of AP Furthermore, the influence of the corresponding V2Os, which was obtained by thermal treatment of VO2(B) nanobelts, on the thermal decomposition of AP was also investigated. The resufs showed that VO2(B) nanobelts had a greater influence on the thermal decomposition temperature of AP than that of V2Os. </abstract>

The influence of vanadium dioxide VO2(B) on thermal decomposition of ammonium perchlorate (AP) has not been reported before. In this contribution, the effect of VO2(B) nanobelts on the thermal decomposition of AP was investigated by the Thermo- Gravimetric Analysis and Differential Thermal Analysis (TG/DTA). VO2(B) nanobelts were hydrothermally prepared using peroxovanadium (V) complexes, ethanol and water as starting materials. The thermal decomposition temperatures of AP in the presence of I wt.%, 3 wt.% and 6 wt.% of as-obtained VO2<B) nanobelts were reduced by 39 °C. 62 °C and 74 °C, respectively. The results indicated that VO2(B) nanobelts had a great influence on the thermal decomposition temperature of AP Furthermore, the influence of the corresponding V2Os, which was obtained by thermal treatment of VO2(B) nanobelts, on the thermal decomposition of AP was also investigated. The resufs showed that VO2(B) nanobelts had a greater influence on the thermal decomposition temperature of AP than that of V2Os.

The influence of VO2(B) nanobelts on thermal decomposition of ammonium perchlorate

School of Chemistry, Dalian University of Technology, Dalian 116024, PR China

Department of English, Dalian Neusoft University of Information, Dalian 116023, PR China

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The influence of VO(B) nanobelts on thermal decomposition of ammonium perchlorate

The influence of vanadium dioxide VO2(B) on thermal decomposition of ammonium perchlorate (AP) has not been reported before. In this contribution, the effect...

The influence of VO₂(B) nanobelts on thermal decomposition of ammonium perchlorate

Published Online: Aug 30, 2016

Page range: 560 - 565

Received: Nov 06, 2014

Accepted: May 18, 2015

DOI: https://doi.org/10.1515/msp-2015-0080

Keywords
VO2(B), ammonium perchlorate, thermal analysis, hydrothermal synthesis

© 2016

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The influence of VO2(B) nanobelts on thermal decomposition of ammonium perchlorate

Published Online: Aug 30, 2016

Page range: 560 - 565

Received: Nov 06, 2014

Accepted: May 18, 2015

DOI: https://doi.org/10.1515/msp-2015-0080

KeywordsVO2(B), ammonium perchlorate, thermal analysis, hydrothermal synthesis

© 2016

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The influence of VO₂(B) nanobelts on thermal decomposition of ammonium perchlorate

Keywords
VO2(B), ammonium perchlorate, thermal analysis, hydrothermal synthesis