Microstructure, Mechanical Properties and Corrosion Behaviour of Iron - Manganese PM Materials Pressed and Sintered Once and Twice

Open access

Abstract

Elemental iron and manganese powders were blended to form mixtures containing 25, 30 and 35wt.% Mn. Mixtures were compressed into prismatic bars and sintered. Some of the bars were repressed and resintered. Compared to a bar pressed and sintered once, the bar pressed and sintered twice possessed a higher relative density, a higher bending stiffness, and a grid microindentation data set with a lower variance. Bars were immersed in Hank's solution for eight weeks. After this procedure, the bending stiffness were found reduced for all bars except for those pressed, sintered and only repressed, the bending stiffness of which remained unchanged. The repressing has most likely closed up throats connecting the clusters of pores with the free surface of a bar, reducing thus a surface area exposed to a corrosive attack. The resintering has opened up those throats, the electrolyte could fill accessible pores and corrosion weakened the near-surface material, reducing thus a bar's bending stiffness.

If the inline PDF is not rendering correctly, you can download the PDF file here.

  • [1] Hermawan H. Dubé D. Mantovani D.: Acta Biomaterialia vol. 6 2010 p. 1693

  • [2] Moravej M. Purnama A. Fiset M. Couet J. Mantovani D.: Acta Biomaterialia vol. 6 2010 p. 1843

  • [3] Xu Z. Hodgson MA. Cao PA.: Materials Science and Engineering: A vol. 630 2015 p. 116

  • [4] Hermawan H.: Biodegradable Metals. From Concept to Application. Heidelberg : Springer 2012

  • [5] Wegener B. Sievers B. Utzschneider S. Müller P. Jansson V. Rößler S. Nies B. Stephani G. Kieback B. Quadbeck P.: Materials Science and Engineering: B vol. 176 2011 p. 1789

  • [6] Witte F.: Acta Biomaterialia vol. 6 2010 p. 1680

  • [7] Xu Z. Hodgson MA. Cao P.: Metals vol. 6 2016 p. 309

  • [8] Kupková M. Hrubovčáková M. Kupka M. Oriňaková R. Morovská Turoňová A.: International Journal of Electrochemical Science vol. 10 2015 p. 9256

  • [9] Kupková M. Hrubovčáková M. Zeleňák A. Sulowski M. Cias A. Oriňáková R. Morovská Turoňová A. Žáková K. Kupka M.: Arch. Metall. Mater. vol. 60 2015 p. 639

  • [10] Kupková M. Hrubovčáková M. Kupka M.: Mater. Sci. Forum vol. 844 2016 p. 46

  • [11] Peng Q. Song Ch. Xia W. Zhai Q. In: TMS 2013 Annual Meeting Supplemental Proceedings. New Jersey : John Wiley & Sons 2013 p. 869

  • [12] Lee YK. Jun JH. Choi CS.: ISIJ Int. vol. 37 1997 p. 1023

  • [13] Danninger H. Gierl C.: Science of Sintering vol. 40 2008 p. 33

  • [14] Hryha E. Dudrová E. Nyborg L.: Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science vol. 41 2010 p. 2880

  • [15] German RM.: Sintering: From Empirical Observations to Scientific Principles. Oxford: Elsevier Butterworth-Heinemann 2014

  • [16] Soboyejo W.: Mechanical Properties of Engineered Materials. New York : Marcel Dekker 2003

  • [17] Su D. He YL. Liu JQ. Lu XG. In: 1st Int. Conference on Information Science Machinery Materials and Energy. Eds. X. Ching V. Dvorik. Chongquing : Atlantis Press Curran Associates Inc 2015 p. 1840

  • [18] Hosford WF.: Iron and Steel. New York : Cambridge University Press 2012

  • [19] Kupková M. Kupka M. Strobl S. Černý M. Khatibi G. Gierl C.: Scripta Materialia vol. 57 2007 p. 639

Search
Journal information
Metrics
All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 240 94 3
PDF Downloads 184 75 1