Evaluation on Curing Properties and Kinetics of Isophthalonitrile Oxide

N,N-dihydroxybenzene-1,3-dicarboximidoyl dichloride was synthesized from benzene-1,3-dicarboxaldehyde and characterized by fourier transform infrared spectroscopy (FT-IR) and nuclear magnetic resonance (1H and 13C NMR). The elastomer was prepared through the 1,3-dipolar cycloaddition of reaction between liquid polybutadiene (LPB) and isophthalonitrile oxide in this work. The tensile strength of different elastomer was enhanced from 0.14 MPa to 0.33 MPa as the elongation at break decreased from 145% to 73%, and the modulus increased from 0.09 kPa to 0.47 kPa. The parameters of kinetic indicated that the curing reaction was fi rst order reaction and the apparent activation energy of each curing system was less than 10.10 kJ/mol when the content of N,N-dihydroxybenzene-1,3- dicarboximidoyl dichloride was increased from 7% to 12%. These results suggested that nitrile oxides achieved curing of polymer binders at room temperature and this work had defi nite guiding signifi cance for the application of nitrile oxides in polymer binders.