Evaluation of the biomedical properties of hydroxyapatite obtained from bone waste
The method of obtaining hydroxyapatite by thermal treatment of deproteinised and defatted bone pulp called bone sludge was presented. The products of the calcining process were characterized with X-ray diffraction (XRD) and Fourier transformed infrared spectroscopy (FT-IR). The calcium content was determined with titration, whereas the contents of total phosphorus - with a spectrophotomertric method. X-ray investigations confirmed that hydroxyapatite was the main component of the calcining products in the calcining process. The FT-IR spectra confirmed that all organic substances were removed during the calcining process. On the basis of the research into physiological liquids the propensity to resorption of hydroxyapatite bioceramic was evaluated.
If the inline PDF is not rendering correctly, you can download the PDF file here.
Święcicki Z. (1992). Bioceramics for orthopedics Instytut Podstawowych Problemów Techniki PAN Wyd. Spółdzielcze Sp. z.o.o. Warszwa (in Polish).
Knychalska-Karwan Z. & Ślósarczyk A. (1994). Hydroxyapatite in stomatology Krakmedia Kraków (in Polish).
Ślósarczyk A. (1997). Hydroxyapatite bioceramics Biuletyn Ceramiczny nr 13 Ceramika 51 Polskie Towarzystwo Ceramiczne Kraków (in Polish).
Shin H. Jo S. & Mikos A.G. (2003). Biomimetic materials for tissue engineering. Biomaterials 24 4353 - 4364.
Vallet-Regi M. & Gonzales-Calbert J. (2004). Calcium phosphates as substitution of bone tissues. Prog. Solid St. Chem. 32 1 - 31. Received 1 December 2003; received in revised form 1 June 2004; accepted 15 July 2004 from Science Direct database on the World Wide Web: www.elsevier.nl/locate/pssc. DOI:10.1016/j.progsolidstchem.2004.07.001. www.elsevier.nl/locate/pssc
Alpert N.L. Kaiser W.E. & Szymański H.A. (1973). Infrared spectroscopy - theory & practice PWN Warszawa (in Polish).
Rapacz-Kmita A. Paluszkiewicz C. Ślósarczyk A. & Paszkiewicz Z. (2005). FTIR and XRD investigations on the thermal stability of hydroxyapatite during hot pressing and pressure less sintering processes J. Mol. Struc. 744 - 747 653 - 656. Received 10 November 2004; accepted 30 November 2004 Available online 11 January 2005 from Science Direct database on the World Wide Web: www.elsevier.com/locate/molstruc. DOI:10.1016/j.molstruc.2004.11.070. www.elsevier.com/locate/molstruc
Ślósarczyk A. Paszkiewicz Z. & Paluszkiewicz C. (2005). FTIR and XRD evaluation of carbonated hydroxyapatite powders synthesized by wet methods J. Mol. Struc 744 - 747 657 - 661. Received 10 November 2004; accepted 30 November 2004 Available online 11 January 2005 from Science Direct database on the World Wide Web: www.elsevier.com/locate/molstruc. DOI: 10.1016/j.molstruc.2004.11.078. www.elsevier.com/locate/molstruc