Study of tungsten surface interaction with plasma streams at DPF-1000U

In this note experimental studies of tungsten (W) samples irradiated by intense plasma-ion streams are reported. Measurements were performed using the modified plasma focus device DPF-1000U equipped with an axial gas-puffing system. The main diagnostic tool was a Mechelle®900 optical spectrometer. The electron density of a freely propagating plasma stream (i.e., the plasma stream observed without any target inside the vacuum chamber) was estimated on the basis of the half-width of the D_β spectral line, taking into account the linear Stark effect. For a freely propagating plasma stream the maximum electron density amounted to about 1.3 × 10¹⁷ cm⁻³ and was reached during the maximum plasma compression. The plasma electron density depends on the initial conditions of the experiments. It was thus important to determine first the plasma flow characteristics before attempting any target irradiation. These data were needed for comparison with plasma characteristics after an irradiation of the investigated target. In fact, spectroscopic measurements performed during interactions of plasma streams with the investigated W samples showed many WI and WII spectral lines. The surface erosion was determined from mass losses of the irradiated samples. Changes on the surfaces of the irradiated samples were also investigated with an optical microscope and some sputtering and melting zones were observed.