The effect of MgB2 addition on the Eu1Ba2Cu3O7 (EBCO) ceramics was systematically studied. Series of Eu1Ba2Cu3O7 + x(MgB2) samples (x = 0 wt.%, 0.05 wt.%, 0.1 wt.%, 1 wt.%, 3 wt.%) were prepared using traditional solid state method. X-ray powder diffraction measurements were used for phase identification. The lattice parameters and orthorombicity decreased with MgB2 addition. A standard four point measurement method was used to determine transition temperatures Tc of superconducting samples. Tc values of the samples were decreasing with MgB2 concentration. TGA results indicate thermal stability of doped samples.