Accelerated cyclic corrosion tests

Open access

Abstract

Accelerated corrosion testing is indispensable for material selection, quality control and both initial and residual life time prediction for bare and painted metallic, polymeric, adhesive and other materials in atmospheric exposure conditions. The best known Neutral Salt Spray (NSS) test provides unrealistic conditions and poor correlation to exposures in atmosphere. Modern cyclic accelerated corrosion tests include intermittent salt spray, wet and dry phases and eventually other technical phases. They are able to predict the material performance in service more correctly as documented on several examples. The use of NSS should thus be restricted for quality control.

1. ČSN EN ISO 9227, Korozní zkoušky v umělých atmosférách – Zkoušky solnou mlhou, Český normalizační institut, 2007.

2. Test method D17 2028, Corrosion test by automatic change of phases of salt spray, drying and humidity (ECC1), Standardisation of Renault Automobiles, DMI / Service 65810, 2007.

3. T. Prošek, M. Kouřil, M. Dubus, M. Taube, V. Hubert, B. Scheffel, Y. Degres, M. Jouannic, D. Thierry, Real-time monitoring of indoor air corrosivity in cultural heritage institutions with metallic electrical resistance sensors, Studies in Conservation 2013, 58, 117–128.

4. SEP 1850, Zyklische Korrosionsprüfung von Werkstoffen und Bauteilen im Automobilbaum / Cyclic corrosion testing of materials and components in automotive construction, 1st Edition, Stahlinstitut VDEh, August 2012.

5. T. Prošek, N. Le Bozec, D. Thierry, Application of automated corrosion sensors for monitoring the rate of corrosion during accelerated corrosion tests, Materials and Corrosion 2014, 65, 448–456.

6. N. LeBozec, N. Blandin, D. Thierry, Accelerated corrosion tests in the automotive industry: A comparison of the performance towards cosmetic corrosion, Materials and Corrosion 2008, 59, 889–894.

7. J. Stoulil, T. Prošek, A. Nazarov, J. Oswald, P. Kříž, D. Thierry: Electrochemical properties of corrosion products on Zn-Al-Mg based coatings, Materials and Corrosion 2015, 66, 777–782.

8. T. Prošek, D. Persson, J. Stoulil, D. Thierry, Composition of corrosion products formed on Zn–Mg, Zn–Al and Zn–Al–Mg coatings in model atmospheric conditions, Corrosion Science 2014, 86, 231–238.

9. N. LeBozec, D. Thierry, P.-E. Augustsson, M. Zapponi, D. Francis, M. Grogna, D. Koberg, L. Opdam, New cyclic test for building coil coated materials, sborník z konference Galvatech 2013, Peking, Čína, příspěvek W019.

10. T. Prošek, N. Larché, M. Vlot, F. Goodwin, D. Thierry, Corrosion performance of Zn–Al–Mg coatings in open and confined zones in conditions simulating automotive applications, Materials and Corrosion 2010, 60, 412–420.

11. T. Koll, F. Beier, T. Boddeker, M. Hinkel, C. Fritzsche, S. Schulz, Performance of a ZM-coating with 1.6% Mg and 1.6% Al in the autobody process chain, SCT 2014, Future trends in steel development, processing technologies and applications, pp. 530–537, Verlag Stahleisen GmbH: Dusseldorf, Německo, 2014.

12. C. Schwerdt, M. Riemer, S. Kohler, B. Schuhmacher, M. Steinhorst, A. Zwick, sborník konference Galvatech‚ 04, Chicago, USA, pp. 783–793, 2004.

13. M. Vlot, R. Bleeker, T. Maalman, E. van Perlstein, Magi-ZincTM, A new generation of hot-dip galvanised products, sborník konference Galvanized Steel Sheet Forum 2006, Düsseldorf, Německo.

Koroze a ochrana materialu

The Journal of Association of Corrosion Engineers (Asociace korozních inženýru)

Journal Information


CiteScore 2017: 0.37

SCImago Journal Rank (SJR) 2017: 0.161
Source Normalized Impact per Paper (SNIP) 2017: 0.489

Metrics

All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 162 162 16
PDF Downloads 79 79 13