Application of the Barkhausen effect probe with adjustable magnetic field direction for stress state determination in the P91 steel pipe

Marek Chmielewski 1  and Leszek Piotrowski 1
  • 1 Gdansk University of Technology, , 80-233, Gdansk

Abstract

The paper presents the results of application of a novel Barkhausen effect (BE) probe with adjustable magnetizing field direction for the stress level evaluation in ferromagnetic materials. The investigated sample was in a form of a pipe, made of P91 steel that was anisotropic due to the production process. The measurements were performed before and after welding, revealing the influence of welding process on the residual stress distribution. As was observed, the process introduced high tensile stresses in the normal to the weld direction (which can be interpreted as a decrease of strongly compressive residual stresses present in martensitic steels). In addition to that, the paper presents investigations of the measurement set performance corroborating its applicability for Barkhausen effect signal measurements in the magnetically anisotropic materials. The signals obtained during manual rotation of the probe (typical method of BE measurements) are very similar to those recorded during automatic field axis rotation.

If the inline PDF is not rendering correctly, you can download the PDF file here.

  • [1] L. Piotrowski, B. Augustyniak, M. Chmielewski and I. Tomas, “The influence of plastic deformation on the magnetoelastic properties of the CSN12021 grade steel”, J.Magn. Magn. Mater., vol. 321 pp. 2331-2335, (2009).

  • [2] O. Stupakov, T. Uchimoto and T. Takagi, “Magnetic anisotropy of plastically deformed low-carbon steel”, J. Phys. D: Appl. Phys., vol. 43 195003 (7p), (2010).

  • [3] C. Gatelier-Rothea, J. Chicois, R. Fougeres and P. Fleischmann, “Characterization of pure iron and (130 ppm) carbon-iron binary alloy by Barkhausen noise measurements: study of the influence of stress and microstructure”, Original Research Article Acta Materialia, vol. 46, no. 14, pp. 4873-4882, (1998).

  • [4] D. C. Jiles, P. Garikepati and D. D. Palmer, “Evaluation of residual stress 300M steels using magnetization, Barkhausen effect and X-ray diffraction techniques”, NDT & E International, vol. 29, no. 5, p. 343, (1996).

  • [5] M. Chmielewski, L. Piotrowski and B. Augustyniak, “A fast procedure of stress state evaluation magnetically anisotropic steels with the help of a probe with adjustable magnetizing field direction”, Measurement, Science and Technology, vol. 28, 045903 (11p), (2017).

OPEN ACCESS

Journal + Issues

Search