Complex Impedance of Manganese Ferrite Powders Obtained by Two Different Methods

Open access

Abstract

Two samples of manganese ferrite powder were obtained by the calcination method (sample A) and hydrothermal method (sample B). The crystal structure of the samples has been determined using X-ray diffraction analysis (XRD). The results shown that the sample A has three phases (FeMnO3, Mn2O3 and Fe2O3) and the prevailing phase is FeMnO3 with perovskite structure and the sample B has only a single phase (MnFe2O4).

The grain morphology was analyzed by scanning electron microscopy (SEM) and the compositional analysis was done by energy dispersive spectroscopy (EDAX).

Measurements of the frequency (f) and temperature (T) dependent complex impedance, Z(f, T) = Z’(f, T) - i Z’’(f, T) of the samples over the frequency range 20 Hz - 2 MHz, at various temperature values from 300C to 1100C are presented. From these measurements, we have shown that the temperature dependence of the relaxation time is of Arhenius type, which suggests that the conduction process is thermally activated. The values obtained for the activation energy Ea, are: 16meV (sample A) and 147.65meV (sample B).

Applying complex impedance spectroscopy technique, the obtained results shows the shape of a single semicircle at each temperature over the measurement range, meaning that the electrical process obeys to a single relaxation mechanism. The impedance and related parameters of the electrical equivalent circuit depend on the temperature and the microstructure of samples. The resistive and capacitive properties of the investigated samples are dominated with the conduction and relaxation processes associated with the grain boundaries mechanism..

[1] E. C. Snelling (editor), Soft Ferrites. Properties and Applications, 2nd (1988) London: Butterworth

[2] S. Sam and A. S. Nesaraj, Int. J. Appl. Sci. Eng., 223 (2011) 223-239

[3] M.A.Ahmed, N.Okasha, S. I. El-Dek, Nanotechnology, 19 (2008) 065-603;

[4] Han Aijun, Liao Juanjuan, Ye Mingquan, Li Yan and Peng Xinhua, Chinese Journal of Chemical Engineering, 19(6) (2011) 1047-1051;

[5] Y.M.Z. Ahmed, Ceramics International, 36 (2010) 969-977

[6] M.M. Rashad, Materials Science & Engineering B, 127, 2-3 (2006) 123-129 |

[7] S.P. Yadav, S.S. Shinde, A.A. Kadam, K.Y. Rajpure, Journal of Alloys and Compounds, 555 (2013) 330-334

[8] A. Lungu, I. Malaescu, C. N. Marin, P. Vlazan, P. Sfirloaga, Physica B: Condensed Matter, 462 (2015) 80-85.

[9] J. T. S. Irvine, D. C. Sinclair, A. R. West, Adv. Mater., 2-3 (2004)132-138

[10] Khalid Mujasam Batoo, Physica B, 406 (2011) 382-387

[11] Khalid Mujasam Batoo, Shalendra Kumar, Chan Gyan Lee, Alimuddin, Journal of Alloys and Compounds, 480 (2009) 596-602.

[12] M. H. Abdullah, A. N. Yusoff, Journal of Materials Science, 32 (1997) 5817Ð5823

[13] S. Khadhraoui, A.Triki, S.Hcini, S.Zemni, M.Oumezzine, Journal of Magnetism and Magnetic Materials, 371(2014) 69-76

[14] Khalid Mujasam Batoo, Shalendra Kumar, Chan Gyu Lee, Alimuddin, Current Applied Physics, 9 (2009) 1397-1406

[15] J. Plocharski, W.Wieczorek, Solid State Ion. 28-30 (1988)979.

[16] M. M. Costa, G. F. M. Pires Jr., A. S. B. Sombra, J. Mater. Chem. Phys,.123 (2010) 35.

[17] J. Hu, H. Qin, J. Magn. Magn. Mater., 231(2001)L1.

[18] B. K. P. Scaife, Principles of dielectrics, Clarendon Press - Oxford, 1998

[19] D. K. Pradhan, B. K. Samantary, R. N. P. Chaudhary, A. K. Thakur, Mater. Sci. Eng. B 116(2005)7.

[20] H. F. Cheng, J. Appl. Phys., 56 (1984) 1831-1837.

Annals of West University of Timisoara - Physics

The Journal of West University of Timisoara

Journal Information

Metrics

All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 88 88 10
PDF Downloads 19 19 3