TEM Microstructure and Chemical Composition of Transition Zone Between Steel Tube and An Inconel 625 Weld Overlay Coating Produced by CMT Method

Open access


The aim of this work was to investigate the microstructure and chemical composition of the transition zone between 16Mo3 steel and Inconel 625 weld overlay coating produced by the Cold Metal Transfer (CMT) method. Investigations were primarily carried out through transmission electron microscopy (TEM) on thin foils prepared by FIB (Focus Ion Beam).

The chemical analysis demonstrated that the amount of certain elements (Fe, Ni, Cr, Mo, Nb) in the transition zone between the base material and the weld overlay changes quickly, from the composition of the steel to the composition of the composite zone. STEM and TEM investigations revealed that two areas are clearly visible in the transition zone. In the narrow band close to the fusion boundary where plates are clearly visible and the Ms temperature is higher than room temperature, electron diffraction analyses show reflections of martensite and austenite. Moreover, the crystallographic relations between martensite and austenite can be described by the Kurdjumov-Sachs (K-S) relationship {110}α{111}γ<11¯1>α<11¯0>γ ). The microstructure of the part of the transition zone with an Ms temperature lower than room temperature as well as that of the composite zone is austenite. The investigations proved that the width of the martensitic area can be significantly limited by using the CMT technique for weld overlaying.

[1] X. Xing, X. Di, B. Wang, The effect of post-weld heat treatment temperature on the microstructure of Inconel 625 deposited metal, J. Alloys Compd. 593, 110-116 (2014).

[2] S.A. David, J.A. Siefert, J.N. DuPont, J.P. Shingledecker, Weldabillity and weld performance of candidate nickel base superalloys for advanced ultrasupercritical fossil power plants part I: fundamentals, Sci. Technol. Weld. Joining. 7, 532-550 (2015).

[3] J.C. Lippold, Welding Metallurgy and Weldability, A John Wiley & Sons, Inc, New Jersey, 2015.

[4] J.N. DuPont, J.C. Lippold, S.D. Kiser, Welding Metallurgy and Weldability of Nickel-Base Alloys, A John Wiley & Sons, INC., Publication, 2009.

[5] J.N. DuPont, Microstructural evolution and high temperature failure of ferritic to austenitic dissimilar welds, Int. Mater. Rev. 4, 208-232 (2012).

[6] J.N. DuPont, C.S. Kusko, Technical Note: Martensite formation in austenitic/ferritic dissimilar alloy welds, Weld. J. 51-54 (2007).

[7] J. Feng, H. Zhang, P. He, The CMT short-circuiting metal transfer process and its use in thin aluminium sheets welding, Mater. Des. 30, 1850-1852 (2009).

[8] C.G. Pickin, S.W. Williams, M. Lunt, Characterisation of the cold metal transfer (CMT) process and its application for low dilution cladding. J. Mater. Process. Technol. 211, 496-502 (2011).

[9] N. Eliaz, A. Shachar, B. Tal, D. Eliezer, Characteristic of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels, Eng. Fail. Anal. 9, 167-184 (2002).

[10] M.D. Rowe, T.W. Nelson, J.C. Lippold, Hydrogen-induced cracking along the fusion boundary of dissimilar metal welds, Weld. J., 31-37 (1999).

[11] A.A. Omar, Effects of welding parameters on hard zone formation at dissimilar metal welds, Research Developments, 86-93 (1998).

[12] B. Zhihui Wang, B. Xu, C. YE, Study of the martensite structure at the weld interface and the fracture toughness of dissimilar metal joints, Weld. Res. Suppl. 397-402 (1993).

[13] C.C. Silva, H.C. de Miranda, M.F. Motta, J.P Farias, Influence of welding in operational conditions on the partial mixed zone formation in Ni-based dissimilar weld overlay, Trends in welding research, The Materials Information Society pp. 336-344, 2012.

[14] B.T. Alexandrov, J.C. Lippold, J.W. Sowards, a. T. Hope, D.R. Saltzmann, Fusion boundary microstructure evolution associated with embrittlement of Ni-base alloy overlays applied to carbon steel, Weld World 57, 39-53 (2012).

[15] G. Li, J. Huang, Y. Wu, An investigation on microstructure and properties of dissimilar welded Inconel 625 and SUS 304 using high-power CO2 laser, Int. J. Adv. Manuf. Technol. 76, 1203-1214 (2015).

[16] M. Rozmus-Górnikowska, M. Blicharski, J. Kusiński, L. Kusiński, M. Marszycki, Influence of boiler pipe cladding techniques on their microstructure and properties. Arch. Metall. Mater. 58, 1993-1996 (2013).

[17] M. Rozmus-Górnikowska, M. Blicharski, J. Kusiński, Metalic Materials 52, 141-147 (2014).

[18] M. Rozmus-Górnikowska, Ł. Cieniek, M. Blicharski, J. Kusiński, Microstructure and microsegregation of an Inconel 625 weld overlay produced on steel pipes by The Cold Metal Transfer technique. Arch. Metall. Mater. 59, 1081-1084. (2014).

[19] M. Rozmus-Górnikowska, M. Blicharski, Microsegregation and precipitates in Inconel 625 arc weld overlay coatings on boiler pipes, Arch. Metall. Mater. 60, 2599-2605 (2015).

[20] B. Mvola, P. Kah, J. Martikainen, Dissimilar ferrous metal welding using advanced gas metal arc welding proceses, Rev. Adv. Mater. Sci. 38, 125-137 (2014).

[21] W. Chung, J. Huang. L. Tsay, Ch. Chen, Microstructure and stress corrosion cracking behaviour of the weld metal in alloy 52-A508 dissimilar welds, Mater. Trans. 52, 12-19 (2011).

[22] Z R. Chen, Y.H. Lu, TEM observations of martensite layer at the weld interface of an A508III to Inconel 82 dissimilar metal weld joint, Metall. Mater. Trans. A 46, 5494-5498 (2015).

Archives of Metallurgy and Materials

The Journal of Institute of Metallurgy and Materials Science and Commitee on Metallurgy of Polish Academy of Sciences

Journal Information

IMPACT FACTOR 2016: 0.571
5-year IMPACT FACTOR: 0.776

CiteScore 2016: 0.85

SCImago Journal Rank (SJR) 2016: 0.347
Source Normalized Impact per Paper (SNIP) 2016: 0.740


All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 342 258 19
PDF Downloads 163 143 17