Magnetic Properties of (Nia-Znb)X Cu1-X Ferrite Nanoparticle Fabricated by Sol-Gel Process

Open access


In future, more mobile devices with different frequencies will be used at the same time. Therefore, it is expected that the trouble caused by wave interference between devices will be further intensified. In order to prevent this trouble, investigation of selective frequency transmission or absorption material is required. In this paper, magnetic properties of nickel-zinc-copper ferrite nano powder was researched as wave absorber. (Nia-Znb)xCu1-xFe2O4(NZCF) nanoparticles were fabricated by the sol-gel method. The influence of copper substitution on lattice parameter change was analyzed by X-ray diffraction (XRD), particle size was analyzed by scanning electron microscopy (SEM), and Magnetic properties analyzed by vibrating sample magnetometer (VSM). The NZCF and Nickel-zinc ferrite (NZF) lattice parameter difference was 0.028 Å and particle size was calculated as 30 nm with the XRD peak. The VSM results of (Ni0.3-Zn0.3)0.6Cu1-0.6Fe2O4 annealed sample at 700°C for 3hous were 58.5 emu/g (Ms), 22.8 Oe (Hc). It was the most suitable magnetic properties for wave absorber in this investigation.

[1] M.E. McHenry, M.A. Willard, D.E. Laughlin, Prog. Mater. Sci. 44, 291-433 (1999).

[2] M.E. McHenry, D.E. Laughlin, Acta Mater. 48, 223-238 (2000).

[3] Y. Yoshizawa, Scripta Mater. 44, 1321-1325 (2001).

[4] Z. Stokłosa, J. Rasek, P. Kwapulinski, G. Badura, G. Haneczok, L. Pajak, J. Lelatko, A. Kolano-Burian, J. Alloy. Compd. 509, 9050-9054 (2011).

[5] G. Herzer, Acta. Mater. 61, 718-734 (2013).

[6] J.H. Nam, H.H. Jung, J.Y. Shin, J.H. Oh, IEEE. T. Magn. 31, 3985-3987 (1995).

[7] C.S. Kim, W.C. Kim, S.Y. An, S.W. Lee, J. Magn. Magn. Mater. 215-216, 213-216 (2000).

[8] T. Nakamura, J. Magn. Magn. Mater. 168, 285 (1997).

[9] F.S. Tehrani, V. Daadmehr, A.T. Rezakhani, R.H. Akbarnejad, S. Gholipour, J. Supercond. Nov. Magn. 25, 2443-2455 (2012).

[10] J.C. Aphesteguy, A. Damiani, D. DiGiovanni, S.E. Jacobo, Physica. B 404, 2713-2716 (2009).

[11] P. Scherrer, Mathematisch-Physikalische Klasse, 2, 98-100 (1918).

Archives of Metallurgy and Materials

The Journal of Institute of Metallurgy and Materials Science and Commitee on Metallurgy of Polish Academy of Sciences

Journal Information

IMPACT FACTOR 2016: 0.571
5-year IMPACT FACTOR: 0.776

CiteScore 2016: 0.85

SCImago Journal Rank (SJR) 2016: 0.347
Source Normalized Impact per Paper (SNIP) 2016: 0.740

Cited By


All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 274 180 15
PDF Downloads 107 84 13