Bimetallic Casting: Ferritic Stainless Steel – Grey Cast Iron

Open access

Abstract

The paper presents the problem of obtaining a permanent diffusional joint between the working surface layer and the base part in a bimetallic casting. The studied bimetallic casting was obtained as a result of using the founding method of layer coating directly in the cast process. The casting prepared using this method consists of two fundamental parts, i.e., the grey cast iron base and the working surface layer which constitutes of X6Cr 13 high-chromium stainless steels plate. Based on the obtained results it was confirmed that the decisive phenomena that are needed to create a permanent joint between the two components of the bimetallic casting are carbon and heat transport from the high-carbon and hot base material which was poured into the mould in the form of liquid metal to the low-carbon and cold material of the working layer which was placed in the mould cavity in the form of a monolithic insert.

[1] S. Žic, I. Džambas, M. Konić, Possibilities of implementing bimetallic hammer castings in crushing industries, Metalurgija 48, 51-54 (2009).

[2] X. Xiao, S. Ye, W. Yin, X. Zhou, Q. Xue, High Cr white cast iron/carbon steel bimetal liner by lost foam casting with liquid-liquid composite process, China Foundry 9, 136-142 (2012).

[3] T. Heijkoop, I. Sare, Cast-bonding – a new process for manufacturing composite wear products, Cast Metals 2, 160-168 (1989).

[4] J. Szajnar, A. Walasek, C. Baron, Tribological and corrosive properties of the parts of machines with surface alloy layer, Archives of Metallurgy and Materials 58, 931-936 (2013).

[5] J. Szajnar, A. Dulska, T. Wróbel, J. Suchoń, Diffusion of C and Cr during creation of surface layer on cast steel casting, Archives of Metallurgy and Materials 59, 1085-1087 (2014).

[6] J. Szajnar, P. Wróbel, T. Wróbel, Multi-layers castings, Archives of Foundry Engineering 10, 181-186 (2010).

[7] T. Wróbel, Ni and Cr base layers in bimetallic castings, 20th Anniversary International Conference on Metallurgy and Materials, May 18-20.2011, Brno, Czech Republic, 758-764.

[8] S. Jura, J. Suchoń, Layered castings sort steel cast iron, Solidification of Metals and Alloys 24, 67-70 (1995), in Polish.

[9] B. Arnold, T. Heijkoop, P. Lloyd, G. Rubens, I. Sare, Wear of cast-bonded components in a coal pulveriser mill, Wear 203-204, 663-670 (1997).

[10] T. Wróbel, Characterization of bimetallic castings with an austenitic working surface layer and an unalloyed cast steel base, Journal of Materials Engineering and Performance 23, 1711-1717 (2014).

[11] W. Wołczyński, T. Himemiya, D. Kopyciński, E. Guzik, Solidification and solid/liquid interface paths for the formation of protective coatings, Archives of Foundry 6, 359-362 (2006).

[12] W. Wołczyński, Z. Pogoda, G. Garzeł, B. Kucharska, A. Sypień, T. Okane, Part I. Thermodynamic and kinetic aspects of the hot dip (Zn) – coating formation, Archives of Metallurgy and Materials 59, 1223-1233 (2014).

[13] P. Duda, J. Taler, Solving direct and inverse heat conduction problems, Springer-Verlag, Berlin Heidelberg 2006.

Archives of Metallurgy and Materials

The Journal of Institute of Metallurgy and Materials Science and Commitee on Metallurgy of Polish Academy of Sciences

Journal Information


IMPACT FACTOR 2016: 0.571
5-year IMPACT FACTOR: 0.776

CiteScore 2016: 0.85

SCImago Journal Rank (SJR) 2016: 0.347
Source Normalized Impact per Paper (SNIP) 2016: 0.740

Cited By

Metrics

All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 278 227 14
PDF Downloads 97 85 4