The conducted studies regarded the analysis of change of structure of point defects occurring during initial stage of recovery of FCC (Al, Cu) and HCP (Ti, Mg and Zn) metals at temperature close to Th =0.5Tm. The changes in resistivity of the deformed and later recovered samples were measured. The recovery time was 1, 2, 3, 4 or 5 min. The observed changes were correlated with reorganization of arrangement of lattice defects during annealing.