Research on the Properties of Co-Tic and Ni-Tic Hip-Sintered Alloys

Open access


Three types of sintered alloys were fabricated based on cobalt, nickel and high-temperature alloy ZhS32-VI matrix with titanium carbide strengthening phase. TiC content was in a range of 30–50 vol. %. The melting temperatures of alloys are higher than 1320°C, and they may undergo undamaged through all technological procedures together with turbine blades, including soldering and outgassing. DSC analyses indicates no additional thermal effects until melting, which confirms their structural stability. The examinations of microstructure revealed three types of constituents – TiC particles, matrix solid solution and blow outs – structural defects having negative effects on all the studied properties. It was found that heat resistance of nickel based sintered alloys at the temperature of 1100°C is superior as compared with the alloys based on cobalt and alloy ZhS32-VI. It has been established that wear resistance in conditions of fretting wear at temperatures of 20, 850, 950 and 1050°C of sintered alloy with ZhS32-VI matrix is mostly superior as compared with the other alloys. The properties of produced alloys allow to use them for manufacturing of components of friction couples operating in conditions of high temperature fretting wear, including protective pads of turbine blades top shrouds contact faces.

If the inline PDF is not rendering correctly, you can download the PDF file here.

  • 1. Babak A. Barsoum M.W. (2016). Energy damping in magnesium alloy composites reinforced with TiC or Ti2AlC particles Materials Science & Engineering A 653 53–62.

  • 2. Babak A. Casi E.N. Barsoum M.W. (2014) Fabrication and mechanical properties of pressureless melt infiltrated magnesium alloy composites reinforced with TiC and Ti2AlC particles Materials Science and Engineering 618 511–522.

  • 3. Baskaran S. Anandakrishnan V Muthukannan Duraisel Vam Keerthivasan N. (2015) Study on dry sliding friction behaviour of tic reinforced AA7075 in-situ composites by Taguchi analysis International Journal of Mechanical And Production Engineering 3(3) 9–12.

  • 4. Bin C. Ye-fa T. Long H. Hua T. Li G. (2013) Tribological properties of TiC particles reinforced Ni-based alloy composite coatings Transactions of Nonferrous Metals Society of China 23(6) 1681–1688.

  • 5. Cherepova T.S. Dmitrieva G.P. (2016a) The Wear Features of Powder Cobalt Alloys Strengthened with Titanium Carbide Powder Metallurgy and Metal Ceramics 55(5-6) 374–378.

  • 6. Cherepova T.S. Dmitrieva G.P. Nosenko A.V. Semirga A.M. (2014) Wear-resistant alloy for protection of contact surfaces of working aircraft engine blades from oxidation at high temperatures Science and Innovation 10(4) 20–28.

  • 7. Cherepova T.S. Dmytrieva H.P. (2016b) Properties of titanium carbide-strenghtened cobalt-based sintered alloys Metal Physics and Advanced Technologies 38(11) 1497–1512 (in Ukrainian).

  • 8. Cherepova T.S. Dmytrieva H.P. Hosenko V.K. (2015) Heat resistance of cast and sintered alloys based on nickel and cobalt strengthened with carbides Metallurgy and Heat Treatment of Metals 3 36–40 (in Ukrainian).

  • 9. Cherepova T.S. Dmitrieva G.P. Nosenko V.K. (2016a). Heat resistance of the powder cobalt alloys reinforced with niobium or titanium carbide Science and Innovation 12(1) 5–10.

  • 10. Cherepova T.S. Dmytrieva H.P. Dukhota O.I. Kindrachuk M.V. (2016b) Properties of nickel powder alloys hardened with titanium carbide Materials Science 52(2) 173–179.

  • 11. Chinmaya K.S. Manoj M. (2015). Effect of pulse laser parameters on TiC reinforced AISI 304 stainless steel composite coating by laser surface engineering process Optics and Lasers in Engineering 67 36–48.

  • 12. Chukwuma C. Onuoha X. Chenxin J. Zoheir N.F. Georges J.K. Kevin P.P. (2016). The effects of TiC grain size and steel binder content on the reciprocating wear behaviour of TiC-316L stainless steel cermets wear Wear 350-351 116–129.

  • 13. Dmitrieva G.P. Cherepova T.S. Kosorukova T.A. Nichiporenko V.I. (2015) Structure and properties of wear resistant cobalt-based alloy with niobium carbide Metal Physics and Advanced Technologies 37(7) 973–986 (in Russian).

  • 14. Dmytrieva H.P. Cherepova T.S. Dukhota O.I. Nychyporenko V.I. (2017) Investigation of properties of sintered alloys based on ZhS32-VI with titanium carbide Powder Metallurgy 11/12 68–75 (in Ukrainian).

  • 15. Dukhota O.I. Tisov O.V. (2010) The study on wear resistance of heat resistant composite alloys in conditions of high temperature fret-ting-wear Problems of friction and wear 53 195–200 (in Ukrainian).

  • 16. Dukhota O.I. Tisov O.V. Cherepova T.S. Dmytrieva H.P. Kharchenko V.V. (2017) Tribotechnical examinations of high temperature wear resistant particle-reinforced alloys Problems of friction and wear 3(76) 60–66 (in Ukrainian).

  • 17. Jung S.-A. Kwon H. Suh C.-Y. Oh J.-M. Kim W. (2015). Preparation of a fine-structured TiC–Co composite by high-energy milling and subsequent heat treatment of a Ti–Co alloy Ceramics International 41(10) 14326–14331.

  • 18. Karantzalis A.E. Lekatou A. Evaggelidou M. (2013) Micro-structure and sliding wear assessment of Co–TiC composite materials International Journal of Cast Metals Research 27(2) 73–79.

  • 19. Levashov E.A. Mishina E.S. Malochkin O.V. Stanskii D.V. Mour J.J. Fadeev M. I. (2003). Effect of nanocrystalline powders on the structure and properties of dispersion-hardened alloy TiC – 40% KhN70Yu Metallurgist 47(3/4) 133–139.

  • 20. Lieontiev V.A. Zilichihis S.D. Kondratiuk Ye.V. Zamkovoi V.Ye. (2006). Recovery of workability of GTE using new technologies and materials Herald of Engine Constructing 4 99–103 (in Russian).

  • 21. Ouyang T. Wu J. Yasir M. Zhou T. Fang X. Wang Y. Liu D. Suo J. (2016) Effect of TiC self-healing coatings on the cyclic oxidation resistance and lifetime of thermal barrier coatings Journal of Alloys and Compounds 656 992–1003

  • 22. Sakamoto T. Kurishita H. Matsuo S. Arakawa H Takahashi S Tsuchida M. Kobayashi S. Nakai K. Terasawa M. Yamasaki T. Kawai M. (2015) Development of nanostructured SUS316L-2%TiC with superior tensile properties Journal of Nuclear Materials 466 468–476.

  • 23. Shuster L.S. Mamleyev R.F. Kamaletdinova R.R. Chertovskikh S.V. Kireev R.M. (2016). Wear of friction pairs made of titanium carbide-based metal–ceramic material Journal of Friction and Wear 37(2) 165–169.

  • 24. Sun-A.J. Hanjung K. Chang-Yul S. Jung-Min O. Wonbaek K. (2015) Preparation of a fine-structured TiC–Co composite by high-energy milling and subsequent heat treatment of a Ti–Co alloy Ceramics International 41 14326–14331.

  • 25. Takahashi S. Ikeno S. Imai E. (1981). Differential thermal analysis and structure of the Ni-TiC system Journal of Materials Science 16(12) 3418–3426.

  • 26. Tretiachenko G.N. Kravchuk G.N. Kuriat R.I. Voloshchenko A.P. (1975) Bearing capacity of gas turbines blades at nonstationary haet and force effect Кyiv.: Naukova Dumka (in Russian).

  • 27. Volkova N. M. Dudorova T. A. Gurevich Y. G. (1989). Influence of hold time on carbide grain growth in TiC-Ni alloys Soviet Powder Metallurgy and Metal Ceramics 28(8) 613–617.

  • 28. Wei Z.(2012). Research on Microstructure and Property of TiC-Co Composite Material Made by Laser Cladding Physics Procedia 25 205–208.

  • 29. Yuxin Li Peikang Bai Yaomin Wang Jiandong Hu Zuoxing Guo (2009). Effect of TiC content on Ni/TiC composites by direct laser fabrication Materials & Design Vol. 30 Iss. 4. 1409–1412.

  • 30. Zhang X.-H. Han J.-C. Du S.-Y. Wood J.V. (2000). Microstructure and mechanical properties of TiC-Ni functionally graded materials by simultaneous combustion synthesis and compaction Journal of Materials Science 35(8) 1925–1930.

  • 31. Zohari S. Sadeghian Z. Lotfi B. Broeckmann C. (2015). Application of spark plasma sintering (SPS) for the fabrication of in situ Ni–TiC nanocomposite clad layer Journal of Alloys and Compounds 633 479–483.

Journal information
Impact Factor

CiteScore 2018: 0.77

SCImago Journal Rank (SJR) 2018: 0.243
Source Normalized Impact per Paper (SNIP) 2018: 0.615

All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 98 98 11
PDF Downloads 76 76 10