Highsilicone Austempered Ductile Iron

Open access


Ductile iron casts with a higher silicone content were produced. The austempering process of high silicone ductile iron involving different austempering times was studied and the results presented. The results of metallographical observations and tensile strength tests were offered. The obtained results point to the fact that the silicone content which is considered as acceptable in the literature may in fact be exceeded. The issue is viewed as requiring further research

[1] Janowiak, J. F. & Gundlach, R. B. (1983). Development of ductile iron for commercial austempering. AFS Transactions. 86, 377.

[2] Röhrig, K. (1983). Zwischenstufenvergütetes Gusseisen mit Kugelgraphit. Giesserei-Praxis. 1/2, 1-13.

[3] Gundalach, R. B. & Janowiak, J. F. (1983). Development of a ductile iron for commercial austempering. AFS Transactions. 94, 377-388.

[4] Harding, R. A. & Gilbert G. N. J. (1986). Why the properties of ductile irons should interest engineers. Br Foundryman. 79. 489-496.

[5] Johansson, M. (1977). Austenitic bainitic ductile iron. AFS Trans. 85, 117-122.

[6] Putatunda, S. K., Bartosiewicz, L., Alberts, F. A. & Singh, I. (1993). Influence of microstructure on high cycle fatigue behavior of austempered ductile cast iron. Mater Charact. 30. 221-234.

[7] Shanmugam, P., Rao, P. P., Udupa, K. R. & Venkataraman, N. (1994). Effect of microstructure on the fatigue strength of an austempered ductile iron. J MaterSci. 29. 4933-4940.

[8] Bartosiewicz, L., Duraiswamy, S., Sengupta, A. Putatunda, S. K. (1991). Near-threshold fatigue crack growth behavior of austempered ductile cast iron. Morris Fine Symposium. (pp. 135-138). Detroit: TMS.

[9] Bartosiewicz, L., Krause, A. R., Duraiswamy, S., Sengupta, A. Putatunda, S. K. (1990). Relationship between fatigue threshold and fatigue strength in austempered ductile cast iron. International Symposium for Testing and Failure Analysis, (pp. 323 -336), vol. 16. ISTFA, ASM.

[10] Rao, P. P. & Putatunda, S. K. (1997). Influence of microstructure on fracture toughness of austempered ductile cast iron. Metal Mater Trans A. 28,1457-1470.

[11] Putatunda, S. K. & Singh, I. (1995). Fracture toughness of unalloyed austempered ductile cast iron. J. Test. Eval. 23(5), 325-332.

[12] Rao, P. P. & Putatunda, S. K. (1998). Dependence of fracture toughness of austempered ductile cast iron on austempering temperature. Meta.l Mater. Trans. A(29), 3005-3016.

[13] Doong, J. L. & Chen, C. (1989). Fracture toughness of bainitic-nodular cast iron. Fatigue Fract Eng Mater Struct. 12, 155-165.

[14] Dorazil, E. Holzman, M. (1991). Fracture behavior of austempered ductile iron. Proceedings of the World Conference on Austempered Ductile Iron, March 1991, (pp. 32-66). Bloomingdale, IL.

[15] Schmidt, I. & Schuchert, A. (1987). Unlubricated wear of austempered ductile cast iron. Z Metal. 78, 871-875.

[16] Bradenberg, K. R., Lee, I., Maxwell, D., Newman P. (2002). Independent Trailer Suspension Utilizing Unique ADI Bracket, SAE Technical Paper 2002-01-0674.

[17] Seaton, P.B., Xiao-Ming, L. (2002). An ADI Alternative for a Heavy Duty Truck Lower Control Arm.

[18] Laino, S., Sikora, J. & Dommarco, R. C. (2011). Advances in the Development of Carbidic ADI, Key Engineering Materials. 457, 187-192.

[19] Raghavendra, H., Bhat, K. L., Rajendra Udupa, K., Rajath Hegde, M. M. (2010). Grinding Wear Behavior of Stepped Austempered Ductile Iron as Media Material During Comminution of Iron Ore in Ball Mills, International Conference on Advances in Materials and Processing Technologies, AMPT, Conference Proceedings eds.: Chinesta F., Chastel Y., and El Mausori M.

[20] Myszka, D., Kaczorowski, M., Tybulczuk, J. (2003). Austempered ductile cast iron directly isothermal tempered, Wyd. Instytutu Odlewnictwa, Kraków.

Archives of Foundry Engineering

The Journal of Polish Academy of Sciences

Journal Information

CiteScore 2016: 0.42

SCImago Journal Rank (SJR) 2016: 0.192
Source Normalized Impact per Paper (SNIP) 2016: 0.316


All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 137 107 6
PDF Downloads 73 67 5