Stress Rupture Test of MAR-M509 Alloy with Structure Refined by Rapid Resolidification

Open access

Abstract

This study presents results of stress rupture test of MAR-M-509 cobalt alloy samples, as-cast and after surface refining with a concentrated stream of heat. Tests were conducted on samples of MAR-M-509 alloy castings, obtained using the lost-wax method. Casting structure refining was performed with the GTAW method in argon atmosphere, using the current I = 200 A and electrical arc scanning velocity vs = 100, 150, 200 and 250 mm/min. The effect of rapid resolidification of the MAR-M-509 alloy on the microstructure was examined and significant improvement in stress rupture test was observed

[1] Klopp, W. D. (1985). Non-Ferrous Alloys. Co. MAR-M-509. Aerospace Structural Metals Handbook.

[2] Rypulak, A. & Orkisz M. (2001). Widmo obciążeń turbinowych silników odrzutowych w trakcie realizacji misji lotniczych. Journal of Koness International CombustionEngines. Wyd. Naukowe Instytutu Lotnictwa.

[3] Orłowicz W. & Trytek A. (2003). Effect of rapid solidification on sliding wear of iron castings. Wear. 254, 154-163.

[4] Orłowicz, W. & Mróz, M. (2003). Microstructure and fatigue strength of A356 alloy casting refined on the surface by rapid crystallization. Zeitschrift fűr Metallkunde. 94, 1320-1326.

[5] Szczotok, A., Szala, J., Cwajna, J., Hetmańczyk, M. & Skupień P. (2005). Effect of cooling speed on primary structure of MAR-M509 cobalt-base superalloy. In Proceedings of 9th European Congress for Stereology and Image Analysis and 7th STERMAT International Conference on Stereology and Image Analysis in Materials Science, Zakopane, 10-13 maj, 2005.

[6] Szala, J., Szczok, A., Richter, J., Cwajna, J. & Maciejny A. (2006). Selection of methods for etching carbides in MARM509 cobalt-base superalloys and acquisition of their images. Materials Characterization. 56, 325-335.

[7] Skupień, P. & Szala, J. (2008). Influence of solution heat treatment parameters on the quantity and morphology of M23C6 carbides in MAR M509 cobalt superalloy. InżynieriaMateriałowa. 4, 358-361.

Archives of Foundry Engineering

The Journal of Polish Academy of Sciences

Journal Information


CiteScore 2016: 0.42

SCImago Journal Rank (SJR) 2016: 0.192
Source Normalized Impact per Paper (SNIP) 2016: 0.316

Metrics

All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 115 113 14
PDF Downloads 74 73 7