Setia Budi, Sukro Muhab, Agung Purwanto, Budhy Kurniawan and Azwar Manaf
The effect of electrodeposition potential on the magnetic properties of the FeCoNi films has been reported in this paper. The FeCoNi electrodeposition was carried out from sulfate solution using potentiostatic technique. The obtained FeCoNi films were characterized by X-ray diffractometer (XRD), atomic absorption spectrometer (AAS) and vibrating sample magnetometer (VSM). It has been shown that the electrodeposition potential applied during the synthesis process determines the magnetic characteristics of FeCoNi films. The more negative potential is applied, the higher Ni content is in the FeCoNi alloy. At the same time, Co and Fe showed almost similar trend in which the content decreased with an increase in applied potential. The mean crystallite size of FeCoNi films was ranging from 11 nm to 15 nm. VSM evaluation indicated that the FeCoNi film is a ferromagnetic alloy with magnetic anisotropy. The high saturation magnetization of FeCoNi film was ranging from 86 A·m2/kg to 105 A·m2/kg. The film is a soft magnetic material which was revealed by a very low coercivity value in the range of 1.3 kA/m to 3.7 kA/m. Both the saturation magnetization and coercivity values decreased at a more negative electrodeposition potential.
Chunyu Deng, Chaoran Qin, Xinyi Li, Shaoqing Li, Zhixiong Huang, Lianmeng Zhang, Xuedong Zhou, Dongyun Guo and Yang Ju
PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.
Grzegorz Tomaszewski, Piotr Jankowski-Mihułowicz, Mariusz Węglarski and Wojciech Lichoń
time of a single process. The reason of such a situation is difficult to explain, but in the source literature, nozzle clogging effects caused by agglomeration of nanoparti-cles in conductive inks and heating of substrate are often indicated [ 14 ].
N1 - 5/14/7 µs 77 V → V=30.1 pL; s = 1.9 m/s
N11 - 5/14/7 µs 77 V → V=22.2 pL; s = 2.2 m/s
N25 - 5/14/7 µs 77 V → V=33.1 pL; s = 1.5 m/s
N47 - 7/8/11 µs 77 V → V=39.2 pL; s = 2.2 m/s
The designed pattern is transferred effectively on a flexiblesubstrate by the drop-on-demand inkjet printing method only when the