Open access

F. Binczyk, P. Gradoń and M. Mańka

Mechanical Properties And Creep Resistance Of Nickel Alloys After Complex Modification And Double Filtration

The paper presents the results of studies to determine the effect of complex surface and bulk modification and double filtration during mould pouring on the stereological parameters of macrostructure and mechanical properties of castings made from the post-production waste IN-713C and the MAR-247 nickel alloys. The evaluation covered the number of grains per 1mm2 of the sample surface area, the average area of grains and the shape index, hardness HB, tensile strength and resistance to high temperature creep. The results indicate the possibility of controlling the stereological parameters of macrostructure through application of several variants of the modification, controlling in this way also different low- and high-temperature properties. The positive effect of double filtration of the alloy during mould pouring on the metallurgical quality and mechanical properties of castings has also been emphasized.

Open access

F. Binczyk and P. Gradoń

Abstract

The paper presents a research results concerning impact of volume modification (ceramic filter containning cobalt aluminate and hafnium powder) and simultaneous surface and volume modification on solidification and stereological parameters of macrostructure of castings made from post-production scrap of nickel superalloy IN-713C. Research included investigation of the influence of chemical composition on the temperature Tliq i Tsol and evaluation of following macrostructure parameters: the number of grains per mm2, average grain area and shape coefficient. Results indicate high influence of carbon content on Tliq. Macrostructure of sample castings indicate positive effect of surface and volume modification, however impact of surface modification is more pronounced.

Open access

F. Binczyk, J. Cwajna and P. Gradoń

Abstract

Paper presents the results of ATD and DSC analysis of two superalloys used in casting of aircraft engine parts. The main aim of the research was to obtain the solidification parameters, especially Tsol and Tliq, knowledge of which is important for proper selection of casting and heat treatment parameters. Assessment of the metallurgical quality (presence of impurities) of the feed ingots is also a very important step in production of castings. It was found that some of the feed ingots delivered by the superalloy producers are contaminated by oxides located in shrinkage defects. The ATD analysis allows for quite precise interpretation of first stages of solidification at which solid phases with low values of latent heat of solidification are formed from the liquid. Using DSC analysis it is possible to measure precisely the heat values accompanying the phase changes during cooling and heating which, with knowledge of phase composition, permits to calculate the enthalpy of formation of specific phases like γ or γ′.

Open access

F. Binczyk, J. Cwajna and P. Gradoń

Abstract

Paper presents the results of research on modified surface grain refinement method used in investment casting of hollow, thin-walled parts made of nickel based superalloys. In the current technology, the refining inoculant is applied to the surface of the wax pattern and then, it is transferred to the ceramic mould surface during dewaxing. Because of its chemical activity the inoculant may react with the liquid metal which can cause defects on the external surface of the cast part. The method proposed in the paper aims to reduce the risk of external surface defects by applying the grain refiner only to the ceramic core which shapes the internal surface of the hollow casting. In case of thin-walled parts the grain refinement effect is visible throughout the thickness of the walls. The method is meant to be used when internal surface finish is less important, like for example, aircraft engine turbine blades, where the hollowing of the cast is mainly used to lower the weight and aid in cooling during operation.

Open access

M. Ciesla, M. Manka, P. Gradon and F. Binczyk

Abstract

The study assesses the impact of surface and bulk modification and filtration during pouring on a durability under accelerated creep conditions of casts made of IN-713C and MAR-247 nickel superalloys scrap used for manufacturing of aircraft engine parts. The impact of solutionizing (1185°C/2 h) with subsequent ageing (870°C/20 h) on the creep resistance of a casting made from MAR-247 coarse-grained superalloy was also examined. Morphological structure parameters were determined with the use of Met-Ilo software. Macrostructure analysis of casts showed very significant impact of surface modification treatment. Creep test results clearly showed that coarse grained samples of IN-713C and MAR-247 superalloys have higher creep resistance. Moreover alloy MAR-247 had higher creep durability after heat treatment compared to as-cast state.

Open access

R. Przeliorz, F. Binczyk, P. Gradoń, M. Góral and T. Mikuszewski

Abstract

Paper presents the results of evaluation of heat resistance and specific heat capacity of MAR-M-200, MAR-M-247 and Rene 80 nickel superalloys. Heat resistance was evaluated using cyclic method. Every cycle included heating in 1100°C for 23 hours and cooling for 1 hour in air. Microstructure of the scale was observed using electron microscope. Specific heat capacity was measured using DSC calorimeter. It was found that under conditions of cyclically changing temperature alloy MAR-M-247 exhibits highest heat resistance. Formed oxide scale is heterophasic mixture of alloying elements, under which an internal oxidation zone was present. MAR-M-200 alloy has higher specific heat capacity compared to MAR-M-247. For tested alloys in the temperature range from 550°C to 800°C precipitation processes (γ′, γ″) are probably occurring, resulting in a sudden increase in the observed heat capacity.

Open access

F. Binczyk, J. Cwajna, P. Gradoń, M. Mańka and R. Findziński

Abstract

In current casting technology of cored, thin walled castings, the modifying coating is applied on the surface of wax pattern and, after the removal of the wax, is transferred to inner mould surface. This way the modification leading to grain refinement occur on the surface of the casting. In thin walled castings the modification effect can also be seen on the other (external) side of the casting. Proper reproduction of details in thin walled castings require high pouring temperature which intensify the chemical reactions on the mould – molten metal interface. This may lead to degradation of the surface of the castings. The core modification process is thought to circumvent this problem. The modifying coating is applied to the surface of the core. The degradation of internal surface of the casting is less relevant. The most important factor in this technology is “trough” modification – obtaining fine grained structure on the surface opposite to the surface reproduced by the core.

Open access

F. Binczyk, J. Cwajna, S. Roskosz and P. Gradoń

Abstract

The paper presents the results of evaluation of the metallurgical quality of master heat ingots and of the identification of non-metallic inclusions (oxides of Al., Zr, Hf, Cr, etc.), which have been found in the shrinkage cavities formed in these ingots. The inclusions penetrate into the liquid alloy, and on pouring of mould are transferred to the casting, especially when the filtering system is not sufficiently effective. The specific nature of the melting process of nickel and cobalt alloys, carried out in vacuum induction furnaces, excludes the possibility of alloy refining and slag removal from the melt surface. Therefore, to improve the quality of castings (parts of aircraft engines), it is so important to evaluate the quality of ingots before charging them into the crucible of an induction furnace. It has been proved that one of the methods for rapid quality evaluation is an ATD analysis of the sample solidification process, where samples are taken from different areas of the master heat ingot. The evaluation is based on a set of parameters plotted on the graph of the dT/dt derivative curve during the last stage of the solidification process in a range from TEut to Tsol.

Open access

F. Binczyk, J. Cwajna, M. Sozańska and P. Gradoń

Abstract

The paper presents the results of research on the impact of impurities in the feed ingots (master heat) on the precipitation of impurities in the ATD thermal analysis probe castings. This impurities occur mostly inside shrinkage cavities and in interdendritic space. Additionally, insufficient filtration of liquid alloy during pouring promotes the transfer of impurities into the casting. The technology of melting superalloys in vacuum furnace prevents the removal of slag from the surface of molten metal. Because of that, the effective method of quality assessment of feed ingots in order to evaluate the existence of impurities is needed. The effectiveness of ATD analysis in evaluation of purity of feed ingots was researched. In addition the similarities of non-metallic inclusions in feed ingots and in castings were observed.

Open access

F. Binczyk, M. Cieśla, P. Gradoń and R. Findziński

Abstract

This paper presents the results of measurements of liquid metal fluidity and linear shrinkage of nickel alloy IN-713C in vacuum induction melting furnace Balzers VSG-2. Because of limited volume of the furnace chamber special models for technological trials were designed and constructed to fit in the mould of dimensions 170x95x100mm. Two different designs of test models were proposed: horizontal round rods and modified spiral. Preliminary studies were carried out for alloys Al-Si. Horizontal round rods test was useful for evaluation of fluidity of hypoeutectic silumin, however in case of nickel superalloy the mould cavity was completely filled in each test because of high required pouring temperature. Positive results were obtained from the modified spiral test for all alloys used in the research. Relationship between the linear shrinkage for the test rod and a specific indicator of contraction defined on a spiral was observed.