Aneta Bartkowska, Dariusz Bartkowski, Damian Przestacki and Małgorzata Talarczyk

Abstract

The paper presents the study results of macro- and microstructure, microhardness and corrosion resistance of C45 medium carbon steel and CT90 high carbon steel after diffusion boriding and laser modification by diode laser. It was found that the increase of carbon content reduced the thickness of boronized layer and caused change in their morphology. Diffusion boronized layers were composed of FeB and Fe2B iron borides. As a result of laser surface modification of these layers, the microstructure composed of three areas: remelted zone, heat affected zone (HAZ) and the substrate was obtained. Microhardness of laser remelting boronized layer in comparison with diffusion boronized layer was lower. The presence of HAZ was advantageous, because mild microhardness gradient between the layer and the substrate was assured. The specimens with laser boronized layers were characterized by better corrosion resistance than specimens without modified layer.

Open access

Aneta Bartkowska, Peter Jurči, Dariusz Bartkowski, Damian Przestacki and Mária Hudáková

Abstract

The paper presents the study results of surface condition, microstructure and microhardness of Vanadis-6 tool steel after diffusion boriding and laser modification by diode laser. As a result of diffusion boriding the layers consisted of two phases: FeB and Fe2B. A bright area under the continuous boronized layers was visible. This zone was probably rich in boron. As a result of laser surface modification of boronized layers, the microstructure composed of three zones: remelted zone, heat affected zone and the substrate was obtained. The microstructure of remelted zone consisted of boron-martensite eutectic. The depth of laser track (total thickness of remelted zone and heat affected zone) was dependent on laser parameters (laser beam power density and scanning laser beam velocity). The microhardness of laser remelting boronized layer in comparison with diffusion boronized layer was slightly lower. The presence of heat affected zone was advantageous, because it allowed to obtain a mild microhardness gradient between the layer and the substrate.