J. Piątkowski, R. Wieszała and A. Gontarczyk

Abstract

The paper presents tribological properties of A390.0 (AlSi17Cu5Mg) alloy coupled in abrasive action with EN-GJL-350 grey cast-iron. The silumin was prepared with the use of two different technologies which differed in terms of cooling speed. In the first case the alloy was modified with foundry alloy CuP10 and cast to a standard tester ATD and in case of second option the modified alloy was cast into steel casting die. Due to different speed of heat removal the silumins varied in structure, particularly with size of primary crystals of silicon and their distribution in matrix which had a significant influence of friction coefficient in conditions of dry friction.

Open access

J. Piątkowski, R. Przeliorz and A. Gontarczyk

Abstract

With the use of differential scanning calorimetry (DSC), the characteristic temperatures and enthalpy of phase transformations were defined for commercial AlSi9Cu3 cast alloy (EN AC-46000) that is being used for example for pressurized castings for automotive industry. During the heating with the speed of 10°C·min−1 two endothermic effects has been observed. The first appears at the temperature between 495 °C and 534 °C, and the other between 555 °C and 631 °C. With these reactions the phase transformation enthalpy comes up as +6 J g−1 and +327 J g−1. During the cooling with the same speed, three endothermic reactions were observed at the temperatures between 584 °C and 471 °C. The total enthalpy of the transitions is – 348 J g−1.

Complimentary to the calorimetric research, the structural tests (SEM and EDX) were conducted on light microscope Reichert and on scanning microscope Hitachi S-4200. As it comes out of that, there are dendrites in the structure of α(Al) solution, as well as the eutectic (β) silicon crystals, and two types of eutectic mixture: double eutectic α(Al)+β(Si) and compound eutectic α+Al2Cu+β.