Open access

B. Grabowska, K. Kaczmarska, A. Bobrowski, Ż. Kurleto-Kozioł and Ł. Szymański

Abstract

The spectroscopic FT-IR and FT-Raman methods allowed to identify the cross-linking process of the aqueous composition of poly(acrylic acid)/sodium salt of carboxymethyl starch (PAA/CMS-Na) applied as a binder for moulding sands (as a novel group binders BioCo). The cross-linking was performed by physical agent, applying the UV-radiation. The results of structural studies (IR, Raman) confirm the overlapping of the process of cross-linking polymer composition PAA/CMS-Na in UV radiation. Taking into account the ingredients and structure of the polymeric composition can also refer to a curing process in a binder - mineral matrix mixture. In the system of binder-mineral matrix under the influence of ultraviolet radiation is also observed effect of binding. However, the bonding process does not occur in the entire volume of the investigated system, but only on the surface, which gives some possibilities for application in the use of UV curing surface of cores, and also to cure sand moulds in 3D printing technology.

Open access

A. Bobrowski, B. Grabowska, S. Żymankowska-Kumon and Ż. Kurleto-Kozioł

Abstract

The article presents research results of physico-chemical and environmental issues for the dust generated during dedusting of the installation for the processing and preparation of moulding sand with bentonite. Particular attention was paid to the content of heavy metals and emission of gases from the BTEX group, which is one of the determinants of the moulding sands harmfulness for the environment. The analysis of heavy metals in the test samples indicate that there is an increase of the content of all metals in the dust compared to the initial mixture of bentonite. The most significant (almost double) increase observed for zinc is probably related to the adsorption of this element on the dust surface by contact with the liquid metal. The study showed, that dust contained more than 20% of the amount of montmorillonite and had a loss on ignition at a similar level. The addition of 1% of dust to the used moulding sand results in almost 30% increase in the total volume of gases generated in casting processes and nearly 30% increase of the benzene emission.