Tribological Properties of PVD Carbon-Copper Composite Films Reinforced by Titanium

Open access

Abstract

Carbon-copper composite coatings reinforced with titanium were deposited using high power magnetron sputtering technique. Tribological and metrological tests were performed using Taylor Hobson Talysurf Intra 50 measuring equipment and CSM Instruments ball-on-disk type tribometer. Friction coefficient and wear rate were determined at 2N, 4N, 6N loads. It was revealed that friction coefficient decreased at a higher Ti concentration, which was particularly expressed at bigger applied loads. However, wear volume values tended to increase in the beginning, till Ti concentration reached about 11 %, but then decreased, thus providing better nanocoating wear resistance.

1. Safi, I. (2000). Recent aspects concerning DC reactive magnetron sputtering of thin films. Surface & Coatings Technology, 127 (2–3), 203–219.

2. Berman, D., Erdemir, A., and Sumant, V. A. (2013). Few layer graphene to reduce wear and friction on sliding steel surfaces. Elsevier, Carbon 54, 454–459.

3. Chan, Y. H., Huang, C. F., Ou, K. L., and Peng, P. W. (2011). Mechanical properties and antibacterial activity of copper doped diamond-like carbon films. Surface & Coatings Technology. 206 (6), 1037–1040.

4. Cabioc’h, T., Naudon, A., Jaouen, M., Thiaudiére, D., and Babonneau, D. (1999). Cosputtering C-Cu thin film synthesis: Microstructural study of copper precipitates encapsulated into a carbon matrix. Philosophical Magazine Part B, 79 (3), 501–516.

5. Musil, J., Louda, M., Soukup, Z., and Kubásek, M. (2008). Relationship between mechanical properties and coefficient of friction of sputtered a-C/Cu composite thin films. Diamond & Related Materials, 17 (11), 1905–1911.

6. Mitin, V., Sharipov, E., and Mitin, A. (2006). High deposition rate magnetrons – innovative coating technology: Key elements and advantages. Surface Engineering, 22 (1), 1–6.

7. Fernández, B., Pereiro, R., Sanz-Medel, A. (2010). Glow discharge analysis of nanostructured materials and nanolayers. Analytica Chimica Acta, 679 (1–2), 7–16.

Latvian Journal of Physics and Technical Sciences

The Journal of Institute of Physical Energetics

Journal Information


CiteScore 2018: 0.32

SCImago Journal Rank (SJR) 2018: 0.147
Source Normalized Impact per Paper (SNIP) 2018: 0.325

Metrics

All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 155 114 17
PDF Downloads 78 65 9