Microstructure Evolution of Ni-Based ODS Superalloy Powders During Horizontal Rotary Ball Milling

Open access

Abstract

Microstructure evolution of Ni-based oxide dispersion-strengthened alloy powders with milling time is investigated. The elemental powders having a nominal composition of Ni-15Cr-4.5Al-4W-2.5Ti-2Mo-2Ta-0.15Zr-1.1Y2O3 in wt % were ball-milled by using horizontal rotary ball milling with the change of milling velocity. Microstructure observation revealed that large aggregates were formed in the early stages of ball milling, and further milling to 5 h decreased particle size. The average crystalline size, estimated by the peak broadening of XRD, decreased from 28 nm to 15 nm with increasing milling time from 1 h to 5 h. SEM and EPMA analysis showed that the main elements of Ni and Cr were homogeneously distributed inside the powders after ball milling of 5 h.

[1] W. Betteridge, S.W.K. Shaw, Mater. Sci. Technol. 3, 682-694 (1987).

[2] D. Furrer, H. Fecht, JOM 51, 14-17 (1999).

[3] T.M. Pollock, S. Tin, J. Propul. Power 22, 361-374 (2006).

[4] S.K. Kang, R.C. Benn, Metall. Trans. A 18, 747-752 (1987).

[5] M. Nganbe, M. Heilmaier, Int. J. Plast. 25, 822-837 (2009).

[6] J.S. Benjamin, Metall. Trans. 1, 2943-2951 (1970).

[7] C. Suryanarayana, Prog. Mater. Sci. 46, 1-184 (2001).

[8] L. Ma, B.S.-J. Kang, M.A. Alvin, C.C. Huang, KONA Powder Part. J. 31, 146-155 (2014).

[9] Y.D. Kim, J.Y. Chung, J. Kim, H. Jeon, Mater. Sci. Eng. A291, 17-21 (2000).

[10] D. Maurice, T.H. Courtney, Metall. Mater. Trans. A 25, 147-158 (1994).

[11] B.D. Cullity, Elements of X-Ray Diffraction, 2nd Ed., New York 1978.

[12] C. Capdevila, H.K.D.H. Bhadeshia, Adv. Eng. Mater. 3, 647-656 (2001).

Archives of Metallurgy and Materials

The Journal of Institute of Metallurgy and Materials Science and Commitee on Metallurgy of Polish Academy of Sciences

Journal Information


IMPACT FACTOR 2016: 0.571
5-year IMPACT FACTOR: 0.776

CiteScore 2016: 0.85

SCImago Journal Rank (SJR) 2016: 0.347
Source Normalized Impact per Paper (SNIP) 2016: 0.740

Metrics

All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 276 276 37
PDF Downloads 149 149 24