Effect of Ultrasonication Dispersion Technique on Sintering Properties of CNT Reinforced Al-Zn-Mg-Cu Powder

Open access


CNT has been researched significantly due to its properties especially mechanical and conductivity properties. Due to strong affinity between particles, dispersion has been remained a problem for its applications. Ultrasonication technique was used to disperse CNT on aluminum powder. Ultrasonication has successfully dispersed CNT on aluminum powder in ethanol. Low energy ball milling for 1h under argon gas with 5:1 ball to powder ratio was used to optimize dispersion of CNT on aluminum. CNT concentration in this research is ranged from 0.1 up to 3wt%. Premix Al-5.5Zn-2.5Mg-0.5Cu powder was used as matrix for this research. Sintering at 580°C for 1h under argon gas was carried to produce high density materials. Pores are still remained on material and it is possibility that pores were caused by agglomeration of CNT. Dispersion high content of CNT is still remained obstacle on this research. Aluminum carbide, Al4C3 is recognized as a ‘bridge between aluminum and CNT for stress transfer was investigated in this research. Raman Spectroscopy, XRD and SEM-EDS were carried out to characterize materials.

[1] H. Kwon, M. Takamichi, A. Kawasaki, M. Leparoux, Mater. Chem. Phys. 138, 787 (2013).

[2] A.M.K. Esawi, K. Morsi, A. Sayed, M. Taher, S. Lanka, Compos. Sci. and Technol. 70, 2237 (2010).

[3] S. Simoes, F. Viana, M.A.L. Reis, M.F. Vieira, Compos. Struct. 108, 992 (2016).

[4] V. Giridhar, R.S. Arunraj, R. Dhisondhar, Inter. J. of Eng. Technol. Research. 1, 54 (2013).

[5] Tao Peng, Isaac Chang, Powder Metallurgy 284, 32 (2015).

[6] A.D.P. LaDelpha, H. Neubing, D.P. Bishop, Mater. Sci. and Eng. A 520, 105 (2009).

[7] H. Rudianto, G.J. Jang, S.S. Yang, Y.J. Kim, I. Dlouhy, Adv. Mater. Sci. Eng., 2015.

Archives of Metallurgy and Materials

The Journal of Institute of Metallurgy and Materials Science and Commitee on Metallurgy of Polish Academy of Sciences

Journal Information

IMPACT FACTOR 2016: 0.571
5-year IMPACT FACTOR: 0.776

CiteScore 2016: 0.85

SCImago Journal Rank (SJR) 2016: 0.347
Source Normalized Impact per Paper (SNIP) 2016: 0.740


All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 192 192 10
PDF Downloads 85 85 3