A thermodynamic description of the Fe-B-Cr system is developed in the context of a new Fe-B-X (X = Cr, Ni, Mn, Si, Ti, V, C) database. The thermodynamic parameters of the binary sub-systems, Fe-B, Fe-Cr and B-Cr, are taken from earlier assessments slightly modifying the Fe-B and B-Cr descriptions, and those of the ternary system are optimized in this study using experimental thermodynamic and phase equilibrium data from the literature. The solution phases are described using substitutional solution model. The borides are treated as stoichiometric or semi-stoichiometric phases and described with two-sublattice models.
 K. Hack, T.G. Char t, Estimation and Critical Assessment of Thermodynamic Data for the B-Cr System, Div. Mater. Appl. Natl. Phys. Lab. Teddington, UK, Comm. Eur. Communities, EUR 7820, Pt. 2, 1982.
 L. Topor, O.J. Kleppa, J. Chem. Thermodyn. 17, 109 (1985).
 H. Kaneko, T. Nishizawa, A. Chiba, Nippon Kinzoku Gakkai-Si. 30, 157 (1966).
 C. Gianoglio, G. Pradelli, Atti Accad. Sci. Torino, Cl. Sci. Fis. Met. Nat. 117, 391 (1985).
 S. Ueno, Y. Waseda, K.T. Jacob, S. Tamaki, Steel Research, 59 (1998) 474-83, by citing “Selected values of thermodynamic properties for steelmaking, The 19th Committee, Japan Society for Promotion and Science, 1984”.
 A.T. Dinsdale, SGTEunary database, version 4.4; www.sgte.org.
 I. Ansara, A.T. Dinsdale, M.H. Rand, COST 507 - Thermochemical database for light metal alloys, Volume 2, European Communities, Belgium, 1998.
 J.-O. Andersson, B. Sundman, CALPHAD 11, 83 (1987).
 J.-O. Andersson, T. Helander, L. Höglund, P. Shi, B. Sundman, CALPHAD 26, 273 (2002).
 P.E. Busby, M.E. Warga, C. Wells, Trans AIME 197, 1463 (1953).
 M.E. Nicholson, Trans AIME 200, 185 (1954).
 C.C. Mc Bride, J.W. Spretnak, R. Speiser, Trans. Amer. Soc. Met. 46, 499 (1954).
 M.L. Borlera, G. Pradelli, Metall. Ital. 65, 421 (1973).
 K. Shirae, Y. Ueda, S. Kachi, K. Kosuge, Mater. Res. Bull. 22, 521 (1987).